Abstract:Nano-LiMn_2O_4 spinel oxides has been prepared successfully by roasting precursor in the air atmosphere, while precursor was obtained by sol-gel techniques, with lithium nitrate and manganese nitrate as original material and citric acid as complexant. The thermal decomposition behavior of the precursor has been examined with the method of DTA-TG. The structure and purity of LiMn_2O_4 powder have been analyzed by means of XRD. The morphology of it also has been observed and grain size has been measured by SEM. The mean valency of manganese in LiMn_2O_4 has been determined by redox titration method. Results show that there're some obvious spinel structure of LiMn_2O_4 at 300 ℃. And the quality of LiMn_2O_4 can be remarkably improved after being pretreated at 300 ℃. The grain size and lattice constant tend to increase with the increase of temperature. After pretreatment, LiMn_2O_4 is in the form of sphericit, distributing evenly with the average grain size of 30 nm. The mean valency of manganese is 3.498, which is very close to the theoretical value.

Study of Preparing Nano-Mn3O4 by Hydrolyzing-oxidizing MnSO4 Directly

Preparation of Mn3 O4 by Alkaline Precipitation-Calcination Process Using MnSO4 Solution

Preparation of nanosized Mn3O4 in oxidative medium of hydrogen peroxide

Preparation and microstructure of nanometer-sized Mn2O3

A simple direct preparation of nanocrystalline γ-Mn2O3 at ambient temperature

Study on microwave-assisted preparation of ultrafine Mn3O4

Synthesis of Nano-LiMnPO4 from MnPO4·H2O Prepared by Mechanochemistry

Preparation of Nano-LiMn2O4

Facile preparation of nanostructured manganese oxides by hydrotreatment of commercial particles

Preparation of MnO_2 Nanorod and Its Catalytic Performance

Preparation Of Nanostructure Mno2 Single Crystal In Various Acid Solution

Synthesis of Nanosized MnOOH Via Solvothermal Route

Preparation of Α-Mn2o3 and MnO from Thermal Decomposition of MnCO3 and Control of Morphology

Preparation of Ultrafine MnO2 Powders by the Solid State Method Reaction of KMnO4 with Mn(II) Salts at Room Temperature

PREPARATION OF NANOSTRUCTURE MnO$_{\bf 2}$ SINGLE CRYSTAL IN VARIOUS ACID SOLUTION

Facile Synthesis of Γ-Mnooh Micro/nanorods and Their Conversion to Β-Mno2, Mn3O4

Room Temperature Synthesis of Mn3O4 Nanoparticles: Characterization, Electrochemical Properties and Hydrothermal Transformation to Γ-Mno2 Nanorods

Preparation of high-purity gamma-Mn3O4 by decomposing MnCO3 from low- grade rhodochrosite ore

Controlled synthesis of Mn3O4 nanocrystallites and MnOOH nanorods by a solvothermal method

Preparation and Electrochemical Performance of Nanostructured MnO2 Materials

Preparation of High-Purity Γ-Mn3o4by Decomposing MnCO3from Low-Grade Rhodochrosite Ore