Research on Preparation and Properties of Solid Buoyancy Materials Filled with Hollow Glass Microspheres

Fanming MENG,Peng WANG,Rui LI,Zhong XIE,Hao WEI,Lianhe LIU

DOI: https://doi.org/10.7502/j.issn.1674-3962.2014.09.10

2014-01-01

Abstract:Solid buoyancy materials with different content of hollow glass microspheres was synthesized by molded form-ing,with bisphenolepoxy resin E5 1 as bulk material,methyl tetrahydrophthalic anhydride as the curing agent,hollow glass microspheres named K25 as lightweight filler.The influence of the content of glass microspheres on density,uniaxial com-pressive strength and resistance to hydrostatic pressure of solid buoyancy material was studied.The results showed that the introduction of microspheres with lower density could reduce the density of solid buoyancymaterial effectively.With the in-creasing of hollow glass microsphere content,the deviation between theoretical density and actual density increased,and the uniaxial compressive strength and resistance to hydrostatic pressure of solid buoyancy material decreased.Especially, when the content of hollow glass microsphere exceeded 18%,the decrease amplitude of the uniaxial compressive strength and resistance to hydrostatic pressure increased.