Abstract:X70 steel, a common pipeline material for the long distance transport, has been extensively used in many domestic and overseas underground projects, for example "West-East" project of P.R. China. In order to study the effect of heavy metal copper(II) on the corrosion performance of X70 steel, electrochemical corrosion tests were conducted on X70 steel in sand soil for 35 d. The macro-/micro-morphology, surface composition, polarization curve, electrochemical impedance spectroscopy (EIS) of X70 steel were characterized by scanning electron microscope (SEM), energy dispersive spectrometer (EDS), and electrochemical workstation, respectively. Five different concentrations of copper(II) were added into the sand soil simulated medium. The macro-/micro-morphology acquired by Canon 6D SLR cameras and SEM. The testing results showed that the copper(II) significantly affected the corrosion performance of X70 steel in sand soil. And corrosion products of X70 steel in sand soil contaminated by copper(II) exhibited colors such as yellow, red-brown, brown, black etc. It was the mixture of compound with Fe, Cu and pure Cu and sand particles. And with the increase of concentration of copper(II) in sand soil, corrosion current density, corrosion rate of X70 steel in sand soil contaminated by copper(II) dramatically increased firstly and then decreased by two orders of magnitude and 0.340% was the threshold, while the corrosion potential positively shifted. At low concentration of copper(II) in sand soil (0.034% and 0.068%), electrochemical impedance spectroscopy (EIS) of X70 steel presented the smaller incomplete capacitive arc in high frequency and the flat capacitive arcs in low frequency. With the concentration sequentially increase of copper(II), the smaller incomplete capacitive arc in high frequency disappeared gradually and the diffusion phenomenon also emerged. Besides, the sum of Rs, Rt and W decreased first and then increased and the minimum value (267.6 Omega) acquired at copper(II) of 0.340%. In general, the addition of increased the corrosion degree of X70 steel in sand soil due to the formation of Cu/Fe micro cell.

Effect of Water Contents in Typical Burma Soil on Corrosion of X70 Steel

Influences of Soil Water Content on Corrosion Behavior of X70 Steel in Yingtan Acidic Soil

Influences of Water Content on the Corrosion Behavior of X70 Steel in Coastal Soil

Effect of Capillarity in Unsaturated Silty Clay on Electrochemical Corrosion Behavior of X70 Steel

Effect of Capillary Water on Electrochemical Corrosion Behaviour and Mechanism of X70 Steel in Silty Clay

Electrochemical Corrosion Behaviour of X70 Steel under the Action of Capillary Water in Saline Soils

CORROSION BEHAVIOUR OF X70 STEEL IN SIMULATED NITRIC ACID RAIN IN ACID SOIL

Electrochemical Corrosion Behaviour of X80 Steel in Sandy Soil under a Natural Air-drying State

A Statistic Study of X70 Steel Corrsion in Sodium Chloride Contaminated Soil

Influence of Simulated Sulfuric Acid Rain on Corrosion Behaviour of X70 Steel in Neutral Soils

Study on Electrochemical Corrosion Behavior of X80 Pipeline Steel in Luoyang Soil with Saturated Water

Macro Non-uniform Corrosion of Q235 Steel in Tropical and Coastal Red Soils

Corrosion Behavior of X80 Steel in Different Simulated Soil Solution

Electrochemical Corrosion Behavior Of X70 Steel In Sand Soil Contaminated By Copper(Ii)

EFFECT OF AGGRESSIVE IONS IN SOILS ON CORROSION BEHAVIOR OF X70 STEEL

Research on the corrosion behaviour of X80 steel in simulative soil solution

Electrochemical Corrosion Behaviour of X70 Steel in Zinc (Ii)-Contaminated Sand Soil

Electrochemcial Corrosion Behavior of X80 Pipeline Steel in Yan'an Soil with Saturated Water

Effect of Microstructures on Corrosion of X80 Pipeline Steel in an Alkaline Soil

Corrosion Behavior and Mechanism of X80 Steel in Silty Soil under the Combined Effect of Salt and Temperature

Corrosion and mass loss behavior of X70 steel in soil contaminated by H2SO4