Influence of Copper Sulphate Concentration on Thermal Control Performance of Micro-Arc Oxidation Coatings on Magnesium Alloy

Chao-nan LI,Qi-xing XIA,Ying WANG,Zhong-ping YAO

DOI: https://doi.org/10.16577/j.cnki.42-1215/tb.2017.10.013

2017-01-01

Abstract:In order to improve the thermal protection of magnesium alloy,the micro-arc oxidation coatings on M B 15 magnesium alloy were prepared by micro-arc oxidation technique in silicate,phosphate and aluminate electrolytes with copper sulphate,respectively.The influences of CuSO4 concentration on the color,thickness,roughness and thermal control performance of coatings were studied by scanning electron microscope,X-ray diffractometer,energy dispersive spectrometer and CIE color system.Results showed that the micro-arc coating possessed typical porous structure.The aluminate coating was mainly composed of MgAl2O4 phase,and the silicate coating was mainly composed of MgO and Mg2SiO4 phases,as well as the phosphate coating was mainly composed of MgO phase.Moreover,the Cu element in coating was formed in the state of amorphous phase.As CuSO4 concentration increased,the color of coatings in three electrolytes changed to black,and the amounts of micro-pores increased.Besides,the coatings prepared in silicate and phosphate electrolytes had the feature of high-absorptance and highemissivity,while the coating prepared in aluminate electrolyte possessed the characteristic of high-absorptance and low-emissivity.