Abstract:The highly filled isotropic polyurethane (PU) elastomer with a magnetorheological (MR) effect was prepared through an in situ polycondensation method. The carbonyl iron particles were treated by coupling agents and then the dispersions of polyol/carbonyl iron particles was prepared by a ball milling process. The dispersion problem of magnetizable particles at a high content in PU matrix was tried to overcome by the combination of surface modification, ball milling, and in situ polymerization. The microstructure and properties of the composite were examined in detail. With increasing the content of carbonyl iron particles, the degree of phase separation of PU increased and the glass transition temperature (T-g) of PU soft segment decreased. Highly filled carbonyl iron particles led to the decrease in the thermal stability of PU matrix, especially in the heating air atmosphere. The MR effect appeared when the content of carbonyl iron particles was higher than 50 wt %, and became relatively pronounced at a 70 wt % of carbonyl iron content. The mechanical properties of PU MR elastomers were deteriorated significantly at a high content of carbonyl iron. Surface modification of carbonyl iron particles can improve the mechanical properties to some extent; however, it was also found that surface modification led to a decrease in the MR effect because of the improved interfacial adhesion. The MR test showed that the maximum absolute MR effect and relative MR effect of PU composite were similar to 0.31 MPa and similar to 8.1% at 1 Hz and 400 mT with 70 wt % of carbonyl iron, respectively. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 114: 901-910, 2009

Study on magnetoresistance properties of polyurethane based magnetorheological gel

Study on the properties of magnetorheological gel based on polyurethane

Study on Off-State Characteristics of Polyurethane Based Magnetorheological Gels

Soft Magnetorheological Polymer Gels with Controllable Rheological Properties

The Influence of the Temperature on the Dynamic Behaviors of Magnetorheological Gel

Influence of Polyurethane Properties on Mechanical Performances of Magnetorheological Elastomers

A high-performance magnetorheological material: Preparation, characterization and magnetic-mechanic coupling properties

The study of natural rubber/polybutadiene rubber hybrid matrix-based magnetorheological elastomer

Anisotropic polyurethane magnetorheological elastomer prepared through in situ polycondensation under a magnetic field

Investigation on magnetorheological elastomers based on natural rubber

New magnetorheological elastomers based on polyurethane/Si-rubber hybrid

Preparation and characterization of isotropic polyurethane magnetorheological elastomer through in situ polymerization

The designation and mechanical properties of magnetorheological plastomer

P-63 Novel Anisotropic Magnetorheological Elastomers

Preparation and Characterization of Magnetorheological Elastomers Based on Natural Rubber

MAGNETORHEOLOGICAL ELASTOMERS BASED ON POLYURETHANE/<font>SI</font>-RUBBER HYBRID

Response Characteristic of the Magnetorheological Plastomer under Different Varying Magnetic Fields

Study on the characteristics of magneto-sensitive electromagnetic wave-absorbing properties of magnetorheological elastomers

Recent Progress on the Magnetorheological Plastomers

Research on Magnetorheological Elastomer Based on Silicone Rubber

High-Performance Hybrid Magnetorheological Materials: Preparation and Mechanical Properties