Research on Kinetics of Magnetization Roasting for Siderite and Hematite Iron Mixtures from Qijiang

Zhang Xiaolong,Han Yuexin,Li Yanjun,Zhou Zheng

DOI: https://doi.org/10.19614/j.cnki.jsks.201802013

2018-01-01

Abstract:Magnetization roasting pretreatment has been proved as an effective method for beneficiation of siderite and hematite iron mixture,the kinetics research on roasting process could provide theoretical support for the key technology of mag-netic roasting for this kind of iron ore.Research of kinetics and roasted product microscopic morphology on magnetization roast-ing for the ore under neutral atmosphere was conducted by X ray diffraction,self-made thermogravimetric analysis furnace and scanning electron microscope.The results showed that the siderite and hematite in ore were transformed into magnetite without any reducers during roasting operation,the resolve occurrence of siderite reaction was the restriction factors of the whole reac-tion process.Increasing heating temperature within a certain range was in favor of shortening the time of each reaction stage, and the maximum conversion rate could be reached with a short time.The mechanism function for magnetization roasting of the ore was nucleation and growth reaction model,the corresponding activation energy E and the pre-exponential factor A were 74.48 kJ/mol and 27.39 min-1respectively.Some micro-cracks were formed in the particles after roasting,iron minerals were closely related to gangue minerals,and fine grinding was required before the further separation.Mn,Ca and Mg remained in roasted product,which could lower the iron grade of the concentrate.