Partial magnetization of siderite via fluidization roasting for efficient recovery of iron: Phase transition, microstructure evolution and kinetics

Qiang Zhang,Yongsheng Sun,Shuai Wang,Yuexin Han,Yanjun Li,Peng Gao

DOI: https://doi.org/10.1016/j.apt.2023.104194

IF: 4.969

2023-10-01

Advanced Powder Technology

Abstract:This study proposes a new process for the partial magnetization of siderite using fluidization roasting, addressing its difficult beneficiation characteristics and lack of large-scale exploitation. Two siderite samples, designated sample S45 and sample S74, with particle sizes of 45–74 μm and 74–150 μm, respectively, were used to optimize the process parameters. The fluidization roasting process rapidly converted siderite to ferromagnetic magnetite, with the magnetite distributed on particle surfaces and internal cracks. CO2 was used during roasting to facilitate the transformation of siderite to magnetite. The iron recovery reached more than 98 % when the roasting time was only 2 min for sample S45 (or 4 min for sample S74). Partial magnetization of siderite can be achieved in a short time by fluidization roasting with low energy consumption for efficient iron recovery. The isothermal kinetics indicate that the kinetic mechanism of the two siderite samples was the random nucleation and growth model, with the fine-grained sample having a shorter reaction time and lower activation energy.

engineering, chemical