Preparation and Mechanical Properties of Modified Na-montmorillonite/Rubber Composite Materials

Xiuyu Liu,Bing Zhang,Hao Zhang

DOI: https://doi.org/10.3969/j.issn.1000-8098.2019.01.004

2019-01-01

Abstract:Cetyl trimethyl ammonium bromide was used to modify Na-montmorillonite. With modified Na-montmorillonite partially replacing carbon black, mixxing carbon black, sulfur, accelerator, zinc oxide, stearic acid, rubber together with modified Na-montmorillonite, modified Namontmorillonite/rubber composite materials were prepared. The results indicate that when ratio of deionized water amount to Na-montmorillonite amount is 35, ratio of cetyl trimethyl ammonium bromide amount to Na-montmorillonite amount is 0.45, the modified Na-montmorillonite/rubber composite materials have the tensile strength of 17.1 MPa, tearing strength of 40.5 kN/m and shore A hardness of 65.7, mechanical performance and economic performance are both good.