Abstract:In this study, open-cell copper foam with completely interconnected sphere pores was prepared by a modified sintering–dissolution process using a preformed calcium chloride template skeleton as space holder. Compared with the traditional foaming process method, the open-cell copper foam prepared by this method has fewer impurities and better surface morphology. In addition, the pore distribution can be controlled by adjusting the distribution of calcium chloride particles in the skeleton. The compression performance, airflow resistance, and filtration performance of the prepared open-cell copper foam were studied. The results show that with the increase in porosity, the bearing capacity of open-cell copper foam decreases, but the width of the stress platform increases. The prepared open-cell copper foam exhibits excellent energy absorption efficiency, reaching nearly 90% at a porosity of 85%. When the porosity is 85%, the static airflow resistance of the structure is as high as 9 KPa·s·m−2. Moreover, the structure has a filtration efficiency of more than 90% as the filtration thickness exceeds 20 mm, which demonstrates the excellent filtration ability. Such open-cell copper foam shows multi-functional potential as an impact damper, sound absorber, and impurity filter.

Copper Foam Preparation by Electrodeposition

Development Status and Preparation Technology of Copper Foams

Preparation of high porosity copper foam by polyurethane sponge impregnation method

Fabrication, Structure and Property of Copper Foam

A Three-Dimensional Cellular Copper Prepared by Multiple-Step Electrodeposition

Bonding Process of Copper Foam-Silver Composite and Performance Characterization of the Joint

Multifunctional Open-Cell Copper Foam with Sphere Pores by a Modified Sintering–Dissolution Process

Effect of bromide ions and polyethylene glycol on morphological control of electrodeposited copper foam

Preparation of Cu-Sn Alloy Foam by Electrodeposition in Acid Solution

Trace Bis-(3-sulfopropyl)-disulfide Enhanced Electrodeposited Copper Foils

New Preparation Technology of Copper Matrix Composites Reinforced by Short Carbon Fibers

Preparation of Metal Foam Using Casting Technology

Microstructure and Sound Absorption of Porous Copper Prepared by Resin Curing and Foaming Method

Mechanical Properties and Microstructure of Rolled and Electrodeposited Thin Copper Foil

Preparation and Heat Dissipation Properties Comparison of Al and Cu Foam

Microstructure and Properties of Porous Copper Foils with High Specific Surface Area Prepared by Electrodeposition

Porous copper with capillary performance and gas permeability prepared by two-step foaming method

Preparation of Aluminum Foam and Influence of Heat Treatment Process

Experimental Study on Capillary Microflows in High Porosity Open-Cell Metal Foams

Effect of additives on the microstructure and properties of pulsed electrodeposited copper foils

A new sintering method for fabrication of open-cell metal foam parts