Granular bainite microstructure evolution and mechanical properties of low carbon steel in quenching isothermal carbon partition process

TIAN Ya-qiang,ZHANG Ming-shan,DONG Fu-tao,LI Hong-bin,WEI Ying-li,CHEN Lian-sheng
DOI: https://doi.org/10.13228/j.boyuan.issn1001-0963.20160249
2017-01-01
Abstract:The influence of different time of carbon partition isothermal quenching treatment at 450 ℃ on the organization and mechanical properties of low carbon Si-Mn steel was investigated by the color metallography,scanning electron microscopy and tensile test method in the I&Q&PB process.The results show that experimental steel microstructure consists essentially of granular bainite and granular structure after various times isothermal carbon partitioning process.When the partition time is in the range of 200-600s,the big block M/A island on grain boundary edge diminishes,but the fine granular M/A island increases and has a gradually increased ordered packing,which results in higher tensile strength and lower elongation.With the extension of carbon partitioning time,fine granular M/A island tends to dispersive arrangement,and the carbide-free lath bainite appears when carbon partition time is longer than the 1 200 s.The film residual austenite between the bainitic ferrite laths is more stable.Under the influence of the fine granular dispersion arrangement M/A islands,the elongation is improved and the tensile strength is decreased.
What problem does this paper attempt to address?