Effects of gradient diffusion and partitioning of carbon in SiMn steel on its microsctructure and mechanical properties

Bozhi Jiang,Fengying Wang,Shuo Cao,Yakun Yao,Songjie Qiao,Huihua Zhou,Yuefeng Zhu

DOI: https://doi.org/10.13251/j.issn.0254-6051.2014.03.001

2014-01-01

Abstract:Microstructure and mechanical properties of steels can be controlled by manipulating the partitioning process of carbon from martensite to austenite , and it becomes an important research direction in the field of iron and steel materials in recent years .Based on the concept of full carbon partitioning , Speer developed a novel process for the heat treatment of steels , that is the quenching and partitioning (Q-P) process.According to analysis on the diffusion and distribution process of carbon in austenite and martensite , stepping-quenching and partitioning ( S-Q-P) process was developed in order to get a better combination of low-carbon martensite , retained austenite and high-carbon martensite , and to enhance the mechanical properties of steels .Mechanical properties tests and microstructure observation have been done to 35SiMn steel treated by Q-T, Q-P and S-Q-P process.The results show that compared to Q-T and Q-P process, the product of strength and ductility of 35SiMn steel is increased by 67% and 32% respectively after S-Q-P process, reaching 31.2 GPa%(1240 MPa ×25%), and microstructure of 35SiMn steel is also close to the designed ideal .All this prove that the microstructure and properties of steels can be controlled by carbon gradient diffusion and partitioning .