Abstract:Phase equilibria and thermodynamic properties of the Ce-Si system were studied experimentally by investigating a Si/(Ce,Si) diffusion couple and thirteen Ce-Si alloys. X-ray diffraction (XRD), electron probe micro-analyzer (EPMA), differential thermal analysis (DTA) and high temperature reaction calorimetry (HTRC) were utilized. A phase with close composition of CeSi1.34 and the decomposition temperature of 1469 K is detected. The eutectic reaction liquid <-> (Si) + CeSi2 is observed to occurs at 1502.6 K. The enthalpy of formation of CeSi1.68 was measured to be -70 +/- 6 kJ mol-atoms(-1). A thermodynamic modeling of the Ce-Si system was then performed by considering the reliable literature data and the present experimental results. A substitutional solution model was used for the description of the liquid phase, and all of the compounds are treated as stoichiometric ones. The calculated phase diagram and thermodynamic properties using the obtained thermodynamic parameters are in good agreement with the experimental data. (C) 2016 Elsevier B.V. All rights reserved.

Experimental investigation of the phase equilibria of the Al-Ce-Ge system at 500 ℃

Phase Equilibria of the Mg-Gd-Ce System at 500 °C

Experimental Investigation of the Al–Ce–Ni System at 800°C

Phase Equilibria in the Al–Zr–Ce System at 773 K

The Phase Equilibria of the Al–Ce–Ni System at 500°C

Investigation of the 600 °C Isothermal Section of the Fe–Al–Ce Ternary System

The Phase Equilibria of the 75 at.% Al-Zn-Ce-Fe Quaternary System at 600 °C

Isothermal Section of Al-Si-Ce Ternary System at 1073 K

A Calorimetric Study of Thermodynamic Properties for Binary Cu–Ge Alloys

Phase Equilibria of the Er-Al-Zr Ternary System at 500 °C

Experimental investigation of phase equilibria in the Al-Ag-Si system

Phase Equilibria of the Ag–Zn–Ce (0–33.3 At.% Ce) System at 450 °C and 600 °C

Phase Equilibria Investigation of the Al–Ni–Er Ternary System at 600 °C and 700 °C

Experimental Investigation and Thermodynamic Modeling of the Ce-Si System

Experimental Investigation of Phase Equilibria in Cu–Ge–Ti System

Phase Equilibria of the Al-Sc-Zr Ternary System at 500 °C

Phase Constitution and Solidification Characteristics of Undercooled Ag-Cu-Ge Ternary Eutectic Alloy

Phase Equilibria of the Al-Co-Er System at 400°C and 600°C

Thermodynamic assessment of Ce-Al system

Experimental Investigation of Phase Equilibrium in the Al–Nb–Hf Ternary System at 600 °C and 400 °C

Experimental Investigation of the Co-Ge Phase Diagram