Abstract:To enhance the ablation resistance of graphite, double-glow plasma surface metallurgy technology was used to efficiently prepare Ta, TaC and Ta/TaC coatings on the graphite. All coatings exhibited a uniform and dense structure, with no microdefects at the interfaces, and the phases of the coatings closely matched the targets. The introduction of the Ta transition layer did not significantly improve the hardness or micro scratch performance of the Ta/TaC coating but greatly enhanced the toughness. Severe ablation occurred on the graphite substrate at 26.5 kW/cm 2 , while noticeable signs of ablation on the Ta and the two TaC coatings was at 61.9 kW/cm 2 and 70.7 kW/cm 2 , respectively. Although the Ta transition layer did not enhance the ultimate failure power of the Ta/TaC coating, notably, the TaC coating lost its protective function after 10 cycles, whereas the Ta/TaC coating remained protective for 15 cycles, exhibiting superior resistance to cyclic ablation. This can be attributed to the Ta transition layer, which not only prevented crack formation and spalling of the Ta/TaC coating but also maintained the integrity of the coating by flowing and filling the TaC coating. Additionally, the Ta oxides formed during the early cycles also provided a certain degree of protection during subsequent ablation tests. The findings of this study can provide an effective approach for the design and fabricating technology of graphite ablation-resistant coatings.

Ablation properties of ZrC coating and ZrC-TaC co-deposition coating Fabricated by CVD

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Phase and microstructure evolutions of in-situ ZrC composite coating under plasma torch ablation

Ablation Resistance of ZrC-based Composite Coating with Multi-Layer Structure for Carbon/carbon Composites above 2200 °C

Fabrication and ablation property of carbon/carbon composites with novel SiC–ZrB2 coating

Oxidation ablation resistance of ZrB2-HfB2-SiC-TaSi2 coating prepared on C/C composite surface

Microstructure and Ablation Behavior of W Coating Prepared by Atmospheric Plasma Spraying for Zr/Cu Infiltrated C/C Composites

High Temperature Oxidation and Oxyacetylene Ablation Properties of ZrB2-ZrC-SiC Ultra-High Temperature Composite Ceramic Coatings Deposited on C/C Composites by Laser Cladding

Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying

Ablation-resistance of ZrB2-SiC Coating under Oxygen-propane Torch Flame Prepared by Atmospheric Plasma Spraying

Preparation and ablation resistance of ZrC nanowires-reinforced CVD-ZrC coating on sharp leading edge C/C composites

Ablation Resistance of C/C Composites with Atmospheric Plasma-Sprayed W Coating

Low-pressure plasma spraying of ZrB2-SiC coatings on C/C substrate by adding TaSi2

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Characteristics of ZrC Barrier Coating on SiC-Coated Carbon/Carbon Composite Developed by Thermal Spray Process

Anti-ablation performance of plasma sprayed ZrB 2 /SiC coatings on C/C substrates and the influence of a chemical vapor deposited SiC interlayer

Ablation of Tungsten Matrix Composites Reinforced by TiC and ZrC Particles

Preparation and long-term ablation behavior of Cf-reinforced ZrC-SiC coated C/C-ZrC-SiC composite

Ablation behavior of Ta, TaC and Ta/TaC coatings on graphite under high-energy laser irradiation

Microstructure and anti-ablation of laser cladding Ti-Zr-B-C coating on TC11 titanium alloy

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments