Microstructure and properties of TiCp/30CrNi4Mo steel-based composites prepared by hot isostatic press

Wenchao FU,Zhiyu XIAO,Shuo YANG,Hangjian GUAN,Liping WEN

DOI: https://doi.org/10.3969/j.issn.1673-0224.2016.04.004

2016-01-01

Abstract:TiCp/30CrNi4Mo steel-based composites were prepared by ball milling and hot isostatic press (HIP). The physical and mechanical properties, including density, hardness, tensile strength at room temperature and high temperature, and wear resistance of composites were investigated. Results show that the composite has fine microstructure with uniform distribution of TiC particles. The TiC particles have a good bonding with the matrix which composed of pearlite, ferrite and a little residual austenite. The relative density, tensile strength, elongation and hardness of the composite are 99.7%, 1 266 MPa, 4.0% and 49 HRC, respectively. The tensile strength of the composite still reaches 1 135 MPa at 400℃, showing good high temperature mechanical property. The wear resistance of the composite increases by 4 times compared with 30CrNi4Mo steel under a load of 200 N. The strength and elongation of the composite reach 1325 MPa and 4.6% after water quenching at 950℃ and tempering at 520℃.