Abstract:A (Fe, Cr)-free Co39.2Ni39.2Al21.6 eutectic medium-entropy alloy (EMEA) was designed and fabricated to study the microstructure and its evolution during slow solidification under different intensities of high static magnetic field (0 T, 5 T and 10 T). It was found that the original microstructure was characterized by FCC/BCC mixed herringbone eutectics consisting of two types of lamellar structures: a curved and wormy anomalous eutectic in the fringe, and a straight and long regular eutectic in the center. Nano-sized L10-type martensite layers are also distributed on the BCC lamellar as the martensitic transformation product. The FCC and BCC phases were enriched in Co and Al elements, respectively, while Ni element was distributed homogenously in both phases. With increasing magnetic field intensity, the herringbone eutectic structures remained stable, without the formation of a primary phase, while the phase constitution and the orientation relationships in the eutectic structures remained unchanged, with no obvious magnetically induced alignments. However, the lamellar spacing of the regular lamellar eutectic decreased significantly from 3.3 μm (0 T) to 1.93 μm (10 T); by contrast, the volume fraction of the anomalous eutectics increased considerably from 28.35% (0 T) to 55.14% (10 T), and the assumption that the imposed convection and destabilization of lamellar eutectics is controlled by the magnetic field is discussed in depth. Our results show a great potential for tailoring microstructures and properties by applying a strong magnetic field during the solidification process of EMEAs.

Solidification Characteristics of Special Alloys under Alternating Magnetic Field

Effect of Electromagnetic Field on Microstructure of Ni-Based Single Crystal Superalloys

Effect of Electromagnetic Stirring on Fine Grain Formation and Tensile Property Improvement for Fe-Ni Superalloy

Magnetic Field-Dependent Microstructure Evolution of Solidified Co39.2Ni39.2Al21.6 Eutectic Medium-Entropy Alloy

Investigations on the Solidification Behavior of Al-Fe-Si Alloy in an Alternating Magnetic Field

Influence of High Magnetic Fields on Phase Transition and Solidification Microstructure in Mn-Sb Peritectic Alloy

Influence of rotating magnetic field driven forced convection on microstructures of Sn-Bialloys

Effect of Magnetic Field During Solidification on Microstructure of Three Al Alloys

Directional Solidification Microstructure of a Ni-Based Superalloy: Influence of a Weak Transverse Magnetic Field

Effect of Horizontal Magnetic Field on the Microstructure of Directionally Solidified Ni-Based Superalloy

Investigation on Macrosegregation and Dendrite Morphology During Directional Solidification of Al-Cu Hypereutectic Alloys under A Strong Magnetic Field

Influence of an Axial Magnetic Field on Microstructures and Alignment in Directionally Solidified Ni-based Superalloy

Study on the Solidification Structures of Al-Fe-Si Alloy under Dc and Ac Magnetic Fields

Temperature field and microstructural formation of semi-solid AlSi7Mg alloy

Effect of an Alternating Magnetic Field on the Microstructure in Hypoeutectic Al-Fe Alloy

Effect of a Transverse Magnetic Field on Solidification Structure in Directionally Solidified Al-40 Wt% Cu Alloys

An experimental instrument for solidification and in situ characterization of the nucleation behavior of high-melting metal under a high magnetic field

Effect of high magnetic field on the primary dendrite arm spacing and segregation of directionally solidified superalloy DZ417G

Influences Of Alternating Magnetic Fieldson The Growth Behavior And Distribution Of The Primary Fe Phasein Cu-14fe Alloys During The Solidification Process

Effects of High Magnetic Fields on Solidification Microstructure of Al–Si Alloys

Liquid State Dependent Solidification of a Co-B Eutectic Alloy under a High Magnetic Field