Abstract:The influence of a high axial magnetic field (up to 6 T) on the solidification structure and crystallography in directionally solidified Al-21.5 wt%Cu-27 wt%Ag and Al-17.6 wt%Cu-42.2 wt%Ag ternary alloys has been systematically studied. Both alloys followed its own typical solidification processes: two-phase univariant eutectic growth (L ->alpha-Al+Al2Cu) and three-phase invariant eutectic growth (L ->alpha-Al-FAl2Cu+Ag2Al) for Al-21.5 wt%Cu-27 wt%Ag and Al-17.6 wt%Cu-42.2 wt%Ag, respectively. It is found that the solidification structure and the orientation relationship (OR) between eutectic phases are modified at lower growth speeds (R <= 3 mu m/s) under the magnetic field (B >= 2 T). For univariant eutectic growth, the magnetic field refines eutectic cell and promotes the transform from cellular structure to planar structure, whereas for invariant eutectic growth, the magnetic field reduces the eutectic spacing and causes the formation of banded structure at lower growth speeds (R <= 0.8 mu m/s). The magnetic field enhances the richness of the Ag solute in the liquid ahead of the quenched liquid/solid interface. In additiOn, the magnetic field modifies the preferred OR between Al2Cu and Ag2Al eutectic phases at lower growth speeds (R <= 3 mu m/s) and induces the formation of the OR with higher interface energy. Modifications of the solidification structure and the OR under the magnetic field are attributed to the thermoelectric magnetic (TEM) effects and the changes in the interfacial energy caused by the magnetic field. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of a Transverse Magnetic Field on Solidification Structure in Directionally Solidified Al-40 Wt% Cu Alloys

Effect of a Transverse Magnetic Field on Solidification Structure in Directionally Solidified Sn–Pb Hypoeutectic Alloys

Investigation on Macrosegregation and Dendrite Morphology During Directional Solidification of Al-Cu Hypereutectic Alloys under A Strong Magnetic Field

Effect of a transverse magnetic field on the growth of equiaxed grains during directional solidification

Effect of a Transverse Magnetic Field on Solidification Structures in Unmodified and Sr-Modified Al-7wtpctSi Alloys During Directional Solidification

EFFECT OF HIGH LONGITUDINAL MAGNETIC FIELD ON THE MICROSTRUCTURE OF DIRECTIONALLY SOLIDIFIED Al-4.5%Cu ALLOY

Effect of a Weak Transverse Magnetic Field on the Morphology and Orientation of Directionally Solidified Al–Ni Alloys

EFFECT OF LONGITUDINAL MAGNETIC FIELD ON THE MICROSTRUCTURE OF DIRECTIONALLY SOLIDIFIED Al-40%Cu HYPEREUTECTIC ALLOY

Effect of a Low Axial Magnetic Field on the Primary Al2Cu Phase Growth in a Directionally Solidified Al–Cu Hypereutectic Alloy

Effect of Multi-Scale Thermoelectric Magnetic Convection on Solidification Microstructure in Directionally Solidified Al-Si Alloys Under a Transverse Magnetic Field

Investigation on the Formation Mechanism of Irregular Dendrite During Directional Solidification of Al–Cu Alloys under a High Magnetic Field

Effect of thermoelectric magnetic force on the array of dendrites during directional solidification of Al–Cu alloys in a high magnetic field

Effect of a High Magnetic Field on the Growth of Ternary Al-Cu-Ag Alloys During Directional Solidification

Effect of a High Axial Magnetic Field on the Structure of Directionally Solidified Al–Si Alloys

Effect of a Weak Transverse Magnetic Field on Solidification Structure During Directional Solidification

Faceted Growth Of Primary Al2cu Crystals During Directional Solidification In High Magnetic Field

Effect of Horizontal Magnetic Field on the Microstructure of Directionally Solidified Ni-Based Superalloy

Effect of a High Magnetic Field on the Growth of Ε-Cuzn5 Dendrite During Directionally Solidified Zn-rich Zn–Cu Alloys

Effect of high magnetic field on solidification microstructure evolution of a Cu-Fe immiscible alloy

Effect of High Longitudinal Magnetic Field on Interface Stability and Morphology of Directionally Solidified Al-0.85％Cu Alloy

Influence of an Axial Magnetic Field on Microstructures and Alignment in Directionally Solidified Ni-based Superalloy