Study on Structure and Mechanical Properties of Epoxy/clay Nanocomposites Prepared by Shear Dispersing Method

LU Hai-jun,LIANG Guo-zheng,ZHANG Bao-yan,CHEN Xiang-bao

DOI: https://doi.org/10.3969/j.issn.1005-5053.2005.03.003

2005-01-01

Abstract:Two comparative processing methods, general stirring with magnetic bar and high shear dispersing with high-speed emulsifying and homogenizing mixer (HEHM), were used to disperse and pulverize clay particles modified with dodecyl amine(DDA) in order to prepare finely exfoliated epoxy/clay nanocomposites. It can be observed from Transmission Electron Microscopy (TEM) graph that large clay aggregates still exist in the cured epoxy/MMT_(DDA) nanocomposites prepared by general dispersing method, only the small clay particles or the external layers of large clay aggregates can be partially exfoliated. While the fine exfoliation can be achieved by exerting external shearing force on clay aggregates and the mechanical properties are dramatically improved. At a constant shearing speed, the mechanical properties are increased with the dispersing time. Impact strength is enhanced to 43.9kJ/m~2 from 32.1kJ/m~2, which is about 36.8% higher than that of pristine epoxy. The flexural strength also can be increased. Dynamic Mechanical Analysis(DMA) indicates that store modulus of epoxy/MMT_(DDA) nanocomposites is not improved in glassy region, but have an increase in glass transition region. The glass transition temperature(T_g) of epoxy/MMT_(DDA)(3wt%) nanocomposites is increased up to 214.9℃ from 209.6℃, which is about 5.3℃ higher than that of pristine epoxy, and the increase of T_g will depends on the dispersion and exfoliation of clay particles.