Influence of forming rate on forming limit of 2219 aluminum alloy under different heat treatment conditions

JIN Chun,HUANG Liang,LI Jian-jun,LIU Xian-long,HONG Xiu-dong

DOI: https://doi.org/10.3969/j.issn.1007-2012.2017.01.021

2017-01-01

Abstract:The uniaxial tensile,plane strain and biaxial tension experiments on 2219 aluminum alloy sheet in fully annealed state and solid solution hardening state were conducted under quasi-static forming and dectromagnetic forming conditions respectively,the forming hmit diagram of 2219 aluminum alloy was established and the forming limit influence law of 2219 aluminum alloy under different heat treatment conditions and forming rates was researched.The results show that the solid solution hardening can significandy increase the strength and reduce the elongation of rupture.The ultimate strain of fully annealed state for quasi-static forming respectively increases by 14.76％,37.98％,39.54％ than that of solid solution hardening state in the above three typical strain states;the ultimate strain of fully annealed state for electromagnetic forming respectively increases by 14.51％,38.03％ and 33.33％ than that of solid solution hardening state in the above three typical strain states;the ultimate strain of full annealed state for electromagnetic forming respectively increases by 16.08％,24.38％ and 18.76％ than that for quasi-static forming in the above three typical strain conditions;the ultimate strain of solid solution hardening state for electromagnetic forming respectively increases by 16.34 ％,24.20％ and 30.94％ than that for quasi-static forming in the above three typical strain conditions.The electromagnetic forming can effectively improve the forming limit and formability of 2219 aluminum alloy.