Effects Of Low Temperature Supersaturation Gaseous Carburization On Mechanical Properties Of 316l Austenitic Stainless Steel

Jiang Yong,Li Yang,Zhang Xian-Cheng,Gong Jian-Ming

DOI: https://doi.org/10.11933/j.issn.1007-9289.20170825002

2018-01-01

China surface engineering

Abstract:Surface hardening of 316L austenitic stainless steels (ASSs) was conducted by low temperature supersaturation gaseous carburization (LTSGC). Carbon content, residual stress and nano-hardness of a LTSGC layer were measured along the depth direction. The plastic strain of the crack initiation on the surface of LTSGC layer was measured by uniaxial tensile tests, and the fracture toughness and average tensile strength of the LTSGC layer were calculated. Results show that a diffusion carbon layer of 30 mu m is formed near the surface of 316L after carburizing at 470 degrees for 30 h. The surface carbon content of the LTSGC layer is up to 2.4%. The nano-hardness of the lager reaches 12.6 GPa, and the compressive residual stress is about -2.2 GPa. The surface fracture toughness and fracture elongation of LTSGC layer surface are about 19 MPa.m1/2 and 1.5%, respectively. The average ultimate tensile strength of the carburizing layer is about 1.4 GPa. The ultimate tensile strength of the samples treated by LTSGC increases while its yield stress slightly decreases.