Effects Of Double Glow Plasma Alloying Ta Layer On Structure And Properties Of Tialn/Ta Composite Coatings

Xu Bin,Liu Zhubo,Zhang Zhilong,Li Shuanping,Yu Shengwang,Zhou Bing
DOI: https://doi.org/10.11933/j.issn.1007-9289.20180831001
2018-01-01
China surface engineering
Abstract:Using metal Ta layer as a transition layer, the TiAlN/Ta composite coatings were prepared by double glow plasma surface alloying (DGPSA) and RF magnetron sputtering (RFMS) with DC pulsed magnetron sputtering technique (DCPMS). The phase structure, surface (cross-section) topography, hardness, adhesion strength, toughness and friction and wear properties of the composite coatings were investigated by grazing incidence X-ray diffraction (GIXRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), nanoindentation, scratches, and friction and wear tests. It is found that the structure of the composite coating is condensed under high bias pressure. The Ta transition layer prepared by RFMS technique has columnar crystal structure. The composite coating has low surface roughness, high hardness and poor wear stability and wear resistance. The Ta transition layer prepared by DGPSA technique has a nanocrystalline structure with increasing surface roughness, decreasing hardness, enhanced wear stability and wear resistance. In contrast, the adhesion and toughness of TiAlN/Ta composite coating are significantly improved by using DGPSA technique to prepare Ta transition layer.
What problem does this paper attempt to address?