Abstract:In order to improve the wear and corrosion resistance of Ti-6Al-4V, a novel beta-Ta2O5 nanoceramic coating was synthesised using reactive sputter deposition enabled by double glow discharge plasma technique. The surface topography, chemical composition, and microstructure of the newly developed coating were characterised by a variety of surface analytical techniques. The coating microstructure was found to exhibit a compact striated pattern extending in a direction perpendicular to coating surface, which is composed of equiaxed beta-Ta2O5 grains with an average grain size of similar to 20 nm, well adhered to the Ti-6A1-4V substrate. The hardness and the Young's modulus of the as-deposited coating were obtained by nanoindentation, and the adhesion strength between the coating and substrate was determined by a scratch tester. The dry sliding wear behaviours of the coating were investigated at room temperature against Si3N4 ceramic balls at room temperature under applied loads ranging from 2.3 N to 5.3 N using a ball-on-disc tribometer. The specific wear rates of the coating exhibited only a slight increase with applied normal load, and were shown to be two orders of magnitude lower than that for Ti-6Al-4V under the same loading condition. Furthermore, the electrochemical behaviour of the coating immersed in 3.5 wt.% NaCl solution was systematically examined by using a range of complementary electrochemical techniques including potentiodynamic polarisation, electrochemical impedance spectroscopy (EIS), MottSchottky analysis as well as potential of zero charge (PZC). The results showed that the corrosion resistance of the beta-Ta2O5 nanoceramic coating was better than that of Ti-6Al-4V alloy in 3.5 wt.% NaCl solution. Hence, by possessing higher mechanical properties and good wear and corrosion resistance, the beta-Ta2O5 nanoceramic coating is considered to be a promising candidate for protection of engineering components operating under harsh conditions. (C) 2016 Elsevier B.V. All rights reserved.

Effect of Plasma Spraying Parameters on Sliding Friction and Wear Behavior of Tantalum Coating

Effect of Plasma Spraying Process on Structure of Ta/W Composite Coating

Effects of plasma spray parameters on structure of Ta/W/Sn multilayer coatings

The Effect of RF Sputtering Power on Structural, Nanomechanical and Tribological Properties of Single Layered TaN Coatings

The Influence of Powder Types and Plasma Spray Conditions on Abrasive Wear of Nanostructured and Conventional Al2o3/Tio2 Coatings

Effect of Ta on the Wear Behavior of Laser Cladding Ni60 Alloy Coatings

Microstructure, Wear Behaviour and Laser Ablation Behaviour of Double Glow Plasma Alloyed Ta-W Coating

Tribological properties and microstructure of monolayer and multilayer Ta coatings prepared by magnetron sputtering

Spraying Power Effect on Micro-Structure and Mechanical Property of TaSi2 Coating Prepared by Supersonic Air Plasma Spraying for SiC-Coated C/C Composites

Preparation and Corrosion Protection of Al2O3-TiO2-Ta Coating on Aluminum Surface by Plasma Spraying

Corrosion and Wear Behaviours of a Reactive-Sputter-deposited Ta2O5 Nanoceramic Coating

The influence of powder types and plasma spray conditions on abrasive wear of nanostructured and conventional Al2O3TiO2 coatings

Tribological Property of Plasma-Sprayed Al2O3-13wt%TiO2 Coatings Onto Resin-Based Composites

Study on Wear Resistance and Spraying Process of Nano-ZrO2 Powder Plasma Spraying Coating

Effect of Nitrogen Doping on Tribological Properties of Ta2O5 Coatings Deposited by RF Magnetron Sputtering

Influence of Ta on Microstructure and Abrasive Wear Resistance of Laser Clad NiCrSiB Coating

Tribological behavior of SAPS sprayed Al2O3-TiO2 and NiCr-Cr3C2 coatings under severe load conditions

Effect of Heat Treatment on LaTi<sub>2</sub>Al<sub>9</sub>O<sub>19</sub>-Zr<sub>0.92</sub>Y<sub>0.08 </sub>O<sub>1.96</sub> Composite Coating Powders by Air Plasma Spraying

Effect of annealing treatment on the microstructure and current carrying tribological properties of in-situ formed TiO2−x coating prepared by plasma spraying

Microstructure and Oxidation Behaviour of Plasma-Sprayed NiCoCrAlY Coatings with and Without Ta on Ti44Al6Nb1Cr Alloys

Plasma sprayed CoNiCrMoNb(BSi) high-entropy amorphous alloy coating: The effect of spraying power on microstructure, mechanical and tribological properties