Effect of inhibition properties of several amino acids on corrosion property of 7B50 aluminium alloy in 1 mol/L NaCl+0.1 mol/L HCl

YANG Biao-biao,SUN Qing-qing,SUN Rui-ji,SHAO Shou-qi,LIU Yang,CHEN Kang-hua
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2015.11.005
2015-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The inhibition behavior of four amino acids for 7B50 aluminium alloy was investigated using the mass loss measurement and electrochemical impedance spectroscopy technique. The corrosion mechanism of amino acid was characterized by corrosion morphologies. The results show that the inhibition efficiency increases with the increase of concentration and the decrease of temperature. The apparent activation energies of aluminium alloys in the presence of amino acids are larger than that of the sample immersed in the blank solution. The apparent activation energies of cysteine(Cys) and methionine (Met) are highest due to the excellent adsorption ability of—SH or—SCH3 groups on the surface of aluminium alloy. The inhibition efficiency of 0.05 mol/L Cys at low temperature is best among these four studied amino acids, e.g., the inhibition efficiency of Cys is 94.7% at room temperature. Met is also S–containing amino acids, but its inhibition efficiency is lower than that of Cys due to the steric hindrance effect. In addition, relatively lower inhibition efficiency is achieved for phenylalanine (Phe). Histidine (His) with low concentration has very bad inhibition performance, however, at higher temperatures, relatively good corrosion inhibition capability of His with high concentration is shown up gradually. The effect of temperature on the inhibition efficiency of Histidine (His) is little. Consequently, the apparent activation energy of Histidine (His) is lower than other amino acids. The corrosion morphologies show that the intercrystalline corrosion and pitting corrosion of aluminium alloys are inhibited in the presence of amino acids.
What problem does this paper attempt to address?