Densification and Mechanical Properties of Hydroxyapatite-Zirconia Composite Materials

LIU Ji-jin,RUAN Jian-ming,Zou Jian-peng

DOI: https://doi.org/10.3321/j.issn:1004-0609.2005.06.023

2005-01-01

The Chinese Journal of Nonferrous Metals

Abstract:Densified HA-ZrO_2 composites were fabricated by adding CaF_2 under pressureless condition. The effects of CaF_2 content on the densification, phase compositions, microstructures and mechanical properties of HA-ZrO_2 composites were investigated. The results show that the reaction between CaF_2 and HA leads to the formation of fluorine partially substituted hydroxyapatite FHA with higher thermal stability, which enhances the densification, microstructures and mechanical properties of HA-ZrO_2 composites. When the HA(10%40%, mass fraction)-ZrO_2 composites adding 6% CaF_2 were sintered at 1350℃ for 4h, their theoretical densities can reach more than 95%. Fractural strength reaches 100200MPa and fracture toughness can enhance 1.21.6MPa·m~(1/2). The effects of zirconia on phase compositions and mechanical properties were also studied. The densities of HA- ZrO_2 composites decrease with increasing ZrO_2 contents. When the mass fraction of CaF_2 is above 6% and that of ZrO_2 is above 40%, formations of CaZrO_3, α-Ca_3(PO_4)_2, HA/ZrO_2 solid solution, and c-ZrO_2 lead to the poorer mechanical property of HA- ZrO_2 composites.