Mechanical Properties of Hydroxyapatite-Zirconia Ceramics As Dental Implant

LI Jing,HUANG Hui,XU Chun,ZHANG Fu-qiang,JIN Xi-hai,GAO Lian

DOI: https://doi.org/10.3969/j.issn.1674-8115.2006.10.003

2006-01-01

Abstract:Objective To obtain the hydroxyapatite(HAp)-zirconia(ZrO_(2))ceramics as dental implant with good mechanical properties. Methods HAp-ZrO_(2) ceramics were obtained with a novel consolidation technique,spark plasma sintering(group A,with constitution 4:6,group B,5:5).The cubage density,three point flexural strength,fracture toughness and hardness were measured.The differences of mechanical properties between the groups were analysed. Results The cubage density,relative density and ratio of pores of group A and group B were(4.87±(0.03))g/cm~(3) vs(4.57±0.05) g/cm~(3),99.47% vs 99.13%,and((3.74)±1.5)% vs(2.54±(1.1)%,) respectively.There were no obvious statistic differences between cubage density and theoretic density of both groups.The three point flexural strength and hardness of group A were significantly greater than those of group B [(598±65) MPa vs(442±31) MPa and(9.7±0.1) GPa vs(9.5±0.1) GPa,respectively,P0.0.1 for both].The fracture toughness was similar between the two groups([2.6±0.2] MPa·m~(1/2) vs [2.5±0.2] MPa·m~(1/2))(P0.0.5).(Conclusion)The larger amount of composition of HAp and lower amount of ZrO_(2) are contained,the lower mechanical properties the HAp-ZrO_(2) ceramics bear.