Atomic Layer Deposition of Zirconia on Titanium Implants Improves Osseointegration in Rabbit Bones
DOI: https://doi.org/10.2147/ijn.s460392
IF: 7.033
2024-05-30
International Journal of Nanomedicine
Abstract:Hong-Joo Kim, 1 Seon-Ki Lee, 2 Hyun-Seung Kim, 3 Won-Jae Kim, 4 Je-Hwang Ryu, 5 Min-Kyung Ji, 6 Hyun-Pil Lim 1 1 Department of Prosthodontics, School of Dentistry, Chonnam National University, Gwangju, Republic of Korea; 2 Department of Prosthodontics, Daejeon Dental Hospital, Wonkwang University, Daejeon, Republic of Korea; 3 KJ Meditech Co., Ltd, Gwangju, Republic of Korea; 4 Department of Oral Physiology, School of Dentistry, Stem cell Secretome Research Center, Chonnam National University, Gwangju, Republic of Korea; 5 Department of Pharmacology and Dental Therapeutics, School of Dentistry, Chonnam National University, Gwangju, Republic of Korea; 6 Dental 4D Research Center, Chonnam National University, Gwangju, Republic of Korea Correspondence: Hyun-Pil Lim, Department of Prosthodontics, School of Dentistry, Chonnam National University, Gwangju, 61186, Republic of Korea, Tel +82-10-2645-7528, Fax +82-62-530-5639, Email Min-Kyung Ji, Dental 4D Research Center, Chonnam National University, Gwangju, 61186, Republic of Korea, Tel +82-10-8432-3639, Fax +82-62-530-5639, Email Purpose: Atomic layer deposition (ALD) is a method that can deposit zirconia uniformly on an atomic basis. The effect of deposited zirconia on titanium implants using ALD was evaluated in vivo. Methods: Machined titanium implants (MTIs) were used as the Control. MTIs treated by sandblasting with large grit and acid etching (SA) and MTIs deposited with zirconia using ALD are referred to as Groups S and Z, respectively. Twelve implants were prepared for each group. Six rabbits were used as experimental animals. To evaluate the osteogenesis and osteocyte aspects around the implants, radiological and histological analyses were performed. The bone-to-implant contact (BIC) ratio was measured and statistically analyzed to evaluate the osseointegration capabilities. Results: In the micro-CT analysis, more radiopaque bone tissues were observed around the implants in Groups S and Z. Histological observation found that Groups S and Z had more and denser mature bone tissues around the implants in the cortical bone area. Many new and mature bone tissues were also observed in the medullary cavity area. For the BIC ratio, Groups S and Z were significantly higher than the Control in the cortical bone area ( P < 0.017), but there was no significant difference between Groups S and Z. Conclusion: MTIs deposited with zirconia using ALD (Group Z) radiologically and histologically showed more mature bone formation and activated osteocytes compared with MTIs (Control). Group Z also had a significantly higher BIC ratio than the Control. Within the limitations of this study, depositing zirconia on the surface of MTIs using ALD can improve osseointegration in vivo. Keywords: atomic layer deposition, ALD, zirconia, machined titanium implant, bone-to-implant contact ratio, BIC, osseointegration Titanium is a biocompatible material mainly used in dental implants. It has mechanical strength and osseointegration capabilities. When titanium is exposed to air, it forms an oxide film, preventing corrosion and promoting osseointegration. 1,2 Titanium dental implants, which were initially machined and used, were reported to have a low success rate depending on bone quality and implantation site. 3,4 Accordingly, various physical and chemical surface treatment methods of titanium implants have been studied to improve osseointegration and increase the implant success rate. 5 One of the implant surface treatment methods is sandblasting with large grit and acid etching (SA), which is a method of spraying metal oxides on dental implant surfaces and then corroding them with acid. This method improves contact area and promotes osseointegration, resulting in a higher clinical success rate. 6,7 However, it has been found to have side effects, including foreign body reaction to the remaining non-absorbable materials and fine cracks on the implant surface due to acid corrosion. 8 Therefore, absorbent or biocompatible materials are sprayed onto the surface, 9 or electrochemical surface treatment methods, including anodized oxidation, are applied. 10 Zirconia (zirconium oxide; ZrO 2 ) is a biocompatible ceramic material with excellent mechanical strength and wear resistance. Since it has little bone resorption caused by bacterial adhesion and does not interfere with the activity of osteoblasts, it has been attracting attention as a potential substitute material for titanium. 11 Since there is a risk of fracture and difficulty in surface treatment when zirconia is used dir -Abstract Truncated-
pharmacology & pharmacy,nanoscience & nanotechnology