Abstract:The wettability, surface topography, surface potential, and degree of order of a homogeneously mixed octyltriethoxysilane (C8TES)/octadecyltrichlorosilane (OTS) self-assembled monolayer (SAM) were characterized by means of contact angle analysis, atomic force microscopy (AFM), electrostatic force microscopy (EFM), and Fourier transform infrared (FTIR) spectroscopy. The formation mechanism of the SAM was studied as the monolayer was constructed using a stepwise approach, taking advantage of the steric hindrance of C8TES. The SAM was found to have a contact angle of 105 and the formation process of the mixed SAM was obviously different from the SAM formation mechanisms of both pure C8TES and OTS. The AFM and EFM characterizations indicated that the mixed SAM had a smooth surface and a homogeneous surface potential distribution with a typical, normal surface potential frequency distribution. The internal structure was highly homogeneous over regions ranging from 500 nm x 500 nm to 20 mu m x 20 pm in size. The FTIR analysis indicated that the mixed SAM had a double-layer film structure, and that the molecular densities were different in the two layers, with the layer closer to the substrate being denser. This work shows that steric hindrance effects can be used to allow the stepwise formation of homogeneously mixed SAMs, and that this method is especially applicable to the construction of the homogeneously mixed SAMs composed of two types of molecules having different head groups.

Effects of Phase Structure on Nano-mechanical Strength of Octadecyltrichlorosilane Molecular Films

Friction and Wear Studies of Octadecyltrichlorosilane SAM on Silicon

Characterization and Tribological Behavior of Octadecene, Dodecene and Undecenoic Acid Films on Si Substrate

Topographical and Performance Characterization of OTS Self-assembled Monolayer on Chemically Textured Silicon Surfaces

Phase Structure and Transitions in A Poly(Methyloctadecylsilane) Oligomer

Preparation and Tribological Behaviors of an Amide-Containing Stratified Self-Assembled Monolayers on Silicon Surface

Friction and fracture properties of polysilicon coated with self-assembled monolayers

STUDY ON MICRO FRICTION AND ADHESION FORCE OF OTS SELF-ASSEMBLED FILM(Ⅱ) EXPERIMENT AND ANALYSIS OF ADHESION FORCE

Experimental Study of Tribological Properties of Silicon-Based MEMS/NEMS Surface with Atomic Force Microscope

Effect of Tetraethoxysilanes (TEOS) on the Nanomechanical Properties of Organic-Inorganic Hybrid Films

Nanoindentation and Deformation Behaviors of Silicon Covered with Amorphous SiO2: a Molecular Dynamic Study

Effect of Thickness of Molybdenum Nano-Interlayer on Cohesion between Molybdenum/Titanium Multilayer Film and Silicon Substrate

OTS Self-Assembled Monolayer on Functionalization Glass and Patterning on Titanium Surface

Characterization of A Homogeneously Mixed Octyltriethoxyilane/Octadecyltrichlorosilane Self-Assembled Monolayer and Analysis of Its Formation Mechanism

Effect of Thickness of Molybdenum Nano-Interlayer on Cohesion between Molybdenum/Titanium Multilayer Film and Silicon Substrate.

EFFECT OF CRYSTALLINE PHASE FORMATION ON OPTICAL PROPERTIES OF TiSi2 THIN FILMS

CHARACTERIZATION OF OCTADECYLTRICHLOROSILANE SELF-ASSEMBLED MULTILAYERS ON PYREX GLASS

Thermal Stability of Octadecyltrichlorosilane and Perfluorooctyltriethoxysilane Monolayers on SiO2

Study on the preparation and nanoindentation of silsesquioxane film derived from(γ- methacryloxypropyl) trimethoxysilanes

Anti-Icing Property of Superhydrophobic Octadecyltrichlorosilane Film and Its Ice Adhesion Strength

Optical and mechanical properties of TiO2/SiO2/organically modified silane composite films prepared by sol–gel processing