Abstract:Air-cooling from an intercritical (IC) temperature produced an acicular pearlite in ferrite structure and was effective in increasing the strength and ductility of ductile iron in sections up to 10 inches (250 mm). Five alloys were melted and poured as 3-inch Y-blocks, and IC heat treatment produced a fine-grained acicular pearlite + ferrite structure in all five alloys. The compositions ranged from 3.39–3.59% C, 2.34–2.45% Si, 0.29–0.44% Mn, 0.59–0.61% Cu and 0.24–1.78 % Ni, with CE ranging from 4.34 to 4.40. Samples were removed from the bottoms of the Y-blocks to obtain test samples for tensile and Charpy V-Notch (CVN) impact testing. The test samples were heat-treated at intercritical temperatures near the upper critical temperature (UCT) and cooled at various rates to simulate air-cooling of castings up to 10 inches (250 mm). Prior to intercritical heat treatment, experiments were conducted to determine the optimum heat treatment parameters. It was found that the path of the thermal cycle on heating to the IC temperature can affect the quality of the heat-treated structure. Among the things learned are the following: The lamellar austenite in ferrite structure persisted at temperatures as high as 60° F above the predicted UCT. Heat treatment at UCT + 20 °F produced the most dense, acicular pearlite + ferrite structure. Ferritizing prior to IC heat treatment minimizes the pearlite network in the cell boundaries. A minimum soak time of 2 h at the IC temperature is recommended. The lamellar structure is stable for at least 8 h. Copper appears to delay the time to reach equilibrium at the UCT. Nickel (at 1.8%) counteracts the Cu effect. The IC heat-treated samples displayed significantly higher ferrite contents over the as-cast materials. The high strength and elongation were attributed to grain refinement and increased ferrite contents, respectively. Furthermore, the material appears to be forgiving of marginal graphite structures. Despite the coarse graphite inclusions with poor shapes, 7–9% elongation was attained in test bars exceeding 60 ksi (414 MPa) yield strength when cooled as a 10-inch (250 mm) section.

Isothermal normalizing process for a ductile iron

Effects of Normalizing and Tempering Temperature on Mechanical Properties and Microstructure of Low Alloy Wear Resistant Steel Casting

Normalizing Temperature Influence on the Microstructure Characteristics, Mechanical and Wear Performance of a Novel High Chromium Cast Iron

Revealing the strength and toughness mechanisms of ductile iron in three heat‐treatment processesUntersuchung der Festigkeits‐ und Zähigkeitsmechanismen von duktilem Eisen in drei Wärmebehandlungsverfahren

Effect of Pre-tempering and Double Normalizing on Microstructure and Mechanical Properties of Low Activation Steel

Achieving Higher Strength and Ductility in Heavy-Section Ductile Iron Castings

Microstructure Feature of Friction Stir Processed Ductile Cast Iron

Microstructure evolution of heavy section ductile iron

High hardness and toughness of white cast iron: The proposal of a novel process

Effect of cyclic quenching treatment on microstructural evolution and properties of ductile cast iron

Tailoring Carbon Distribution in Α/γ Phase of Ductile Iron and Its Effects on Thermal Conductivity

Effect of the Austenitizing Temperature on Microstructure Evolution and Impact Toughness of a Novel Bainite Ductile Iron

Microstructures, Compressive Residual Stress, Friction Behavior, and Wear Mechanism of Intensive Quenched Ductile Iron

Effects of Normalizing Processes on Microstructure and Impact Toughness in Ti-Bearing Weld Metal of Multi Layer Mag Welded Hsla Steel

Mechanical Properties and Fracture Toughness Prediction of Ductile Cast Iron under Thermomechanical Treatment

Effects of Quenching Medium on Microstructure and Mechanical Properties of High Chromium Cast Iron

Development of New Ductile Iron with Super-High Thermal Conductivity and Elongation

The effect of isothermal holding on the microstructures and mechanical properties of a low carbon alloy steel

Effect of regular thicknesses on the microstructural and quantitative analysis for a hypo-eutectic ductile iron alloyed with Ni and V

Effect of quenching temperature on microstructure and properties of multivariate high chromium cast iron

Mechanism Analysis for the Enhancement of Low-Temperature Impact Toughness of Nodular Cast Iron by Heat Treatment