Effect of Gd content on microstructure and properties of Mg-Gd-Y-Zr alloy

CHEN Xiao-ya,LI Quan-an,CHEN Jun,MENG Bo-bo

DOI: https://doi.org/10.13289/j.issn.1009-6264.2017-0335

2017-01-01

Abstract:Microstructure of as cast,solid solution and aged Mg-xGd-2Y-0.5Zr (x =9,11,13,15 mass％) alloy and longitudinal section near tensile fracture surface were observed and analyzed by optical microscope.The fracture morphology and mechanical properties of the alloy at different temperatures were measured and analyzed by SEM and tensile test machine,respectively.The results show that after solid solution at 525 ℃ for 6 h and aging at 225 ℃ for 10 h,the bulk dendrites of the as-cast Mg-13Gd-2Y-0.5Zr alloy disappear,and the grain boundaries are clearly visible.When the content of Gd is 13 mass％,the grain of the alloy is finer and the microstructure distribution is homogeneous;Mg-13Gd-2Y-0.5Zr alloy has excellent mechanical properties at room temperature and high temperature,and the tensile strength of the alloy reaches maximum value at room temperature and high temperature.When the content of Gd is constant,the tensile strength of the alloy increases first and then decreases with the increasing of tensile temperature,and reaches the maximum at 250 ℃.The fracture mechanism of the Mg-13Gd-2Y-0.5Zr alloy is brittle fracture,and intergranular fracture is dominant.