Abstract:Directional solidification of A1-4.5Cu alloy refined by adding Al-5Ti-1B has been carried out to investigate the texture formation and grain boundary characteristic of the paramagnetic crystal under a high magnetic field. OM and EBSD were applied to analyze the microstructures solidified at different temperature gradients (G) and magnetic field intensities (B). The results show that at the temperature gradient of 27 K/cm; the orientations of fcc alpha-Al grains without magnetic field are random. However, as a high magnetic field is imposed, the easy magnetization axes < 310 > of the alpha-Al grains are aligned parallel to the direction of the magnetic field leading to < 310 > texture. Meanwhile, the ratio of coincidence site lattice (CSL) grain boundaries increases with the increment of magnetic field intensity and reaches its maximum value at 4 T, but decreases as the magnetic field enhances further. On the other hand, when the temperature gradient is elevated, columnar dendrite morphology is exhibited without magnetic field; while a 6 T high magnetic field is introduced, the columnar dendrites are broken and equiaxed grains of random orientations are obtained. The alignment behavior of the free crystals in melt could be attributed to the magnetic crystalline anisotropy of alpha-Al. Moreover, the influence of fluid flow on the texture formation and CSL grain boundary development under magnetic field is discussed. The absence of convection is benefit for grain reorientation and CSL boundary formation. The application of high static magnetic field will inhibit the macro-scale convection. However, the interaction between thermoelectric current and magnetic field will cause micro-scale fluid flow, i.e., thermoelectric magnetic convection (TEMC). The TEMC will give rise to perturbation near the solid-liquid interface leading to the appearance of freckles as well as the decreasing of the ratio of CSL boundary. Moreover, it is proposed that the formation of CSL boundary is associated with the rotation of the free grains in melt along specific crystallographic axes by magnetic torque.

Influences of Rectangular Wave Magnetic Field on Solidification Structure and Properties of 7A04 Aluminum Alloy

Texture Formation and Grain Boundary Characteristic of A1-4.5cu Alloys Directionally Solidified under High Magnetic Field

Effects of DC Magnetic Field on Crystal Orientation and Mechanical Properties of Al-4.5Cu Alloy

Research situation and prospect of influence of electromagnetic field on the solidification structure of aluminum and magnesium alloys

Effect on microstructure and corrosion resistance of semi-solid slurry of 7A04 aluminum alloy by electromagnetic stirring

Effect of a Transverse Magnetic Field on Solidification Structure in Directionally Solidified Al-40 Wt% Cu Alloys

Effect of DC Magnetic Field on Crystal Orientation and Mechanical Properties of Pure Aluminum

Influence of static magnetic field on rapid solidified structure and nanocrystallization behavior of Fe-Si-B-Cu soft magnetic alloys with pre-existing α-Fe nanocrystals

EFFECT OF HIGH LONGITUDINAL MAGNETIC FIELD ON THE MICROSTRUCTURE OF DIRECTIONALLY SOLIDIFIED Al-4.5%Cu ALLOY

Effect of Magnetic Field on Solidification Microstructure of Cu-20wt%Nb Alloys and Properties of the In-Situ Deformed Wires

Effect of a Transverse Magnetic Field on Solidification Structures in Unmodified and Sr-Modified Al-7wtpctSi Alloys During Directional Solidification

Effects of solid solution treatment on microstructure and mechanical properties of 7A09 aluminum alloy

Magnetic field treatment effects on microstructure and properties of A356 aluminium alloy

EFFECT OF LONGITUDINAL MAGNETIC FIELD ON THE MICROSTRUCTURE OF DIRECTIONALLY SOLIDIFIED Al-40%Cu HYPEREUTECTIC ALLOY

Influence of the magnetic field on the microstructure of AZ91 magnesium alloy

Influences Of Alternating Magnetic Fieldson The Growth Behavior And Distribution Of The Primary Fe Phasein Cu-14fe Alloys During The Solidification Process

Effect of Multi-Scale Thermoelectric Magnetic Convection on Solidification Microstructure in Directionally Solidified Al-Si Alloys Under a Transverse Magnetic Field

Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe Alloy

Effect of a High Axial Magnetic Field on the Structure of Directionally Solidified Al–Si Alloys

Effect of a transverse magnetic field on the growth of equiaxed grains during directional solidification

Effect of Magnetic Field on Solidification Structure of A Centrifugal Cast High Speed Steel Roll