Abstract:Directional solidification of A1-4.5Cu alloy refined by adding Al-5Ti-1B has been carried out to investigate the texture formation and grain boundary characteristic of the paramagnetic crystal under a high magnetic field. OM and EBSD were applied to analyze the microstructures solidified at different temperature gradients (G) and magnetic field intensities (B). The results show that at the temperature gradient of 27 K/cm; the orientations of fcc alpha-Al grains without magnetic field are random. However, as a high magnetic field is imposed, the easy magnetization axes < 310 > of the alpha-Al grains are aligned parallel to the direction of the magnetic field leading to < 310 > texture. Meanwhile, the ratio of coincidence site lattice (CSL) grain boundaries increases with the increment of magnetic field intensity and reaches its maximum value at 4 T, but decreases as the magnetic field enhances further. On the other hand, when the temperature gradient is elevated, columnar dendrite morphology is exhibited without magnetic field; while a 6 T high magnetic field is introduced, the columnar dendrites are broken and equiaxed grains of random orientations are obtained. The alignment behavior of the free crystals in melt could be attributed to the magnetic crystalline anisotropy of alpha-Al. Moreover, the influence of fluid flow on the texture formation and CSL grain boundary development under magnetic field is discussed. The absence of convection is benefit for grain reorientation and CSL boundary formation. The application of high static magnetic field will inhibit the macro-scale convection. However, the interaction between thermoelectric current and magnetic field will cause micro-scale fluid flow, i.e., thermoelectric magnetic convection (TEMC). The TEMC will give rise to perturbation near the solid-liquid interface leading to the appearance of freckles as well as the decreasing of the ratio of CSL boundary. Moreover, it is proposed that the formation of CSL boundary is associated with the rotation of the free grains in melt along specific crystallographic axes by magnetic torque.

Texture Formation and Grain Boundary Characteristic of A1-4.5cu Alloys Directionally Solidified under High Magnetic Field

Faceted Growth Of Primary Al2cu Crystals During Directional Solidification In High Magnetic Field

High-Magnetic-Field-Induced Formation of Aligned Equiaxed Grains During Directional Solidification

EFFECT OF HIGH LONGITUDINAL MAGNETIC FIELD ON THE MICROSTRUCTURE OF DIRECTIONALLY SOLIDIFIED Al-4.5%Cu ALLOY

Constitutional supercooling and corresponding microstructure transition triggered by high magnetic field gradient during directional solidification of Al-Fe eutectic alloy

Effect of Multi-Scale Thermoelectric Magnetic Convection on Solidification Microstructure in Directionally Solidified Al-Si Alloys Under a Transverse Magnetic Field

Effect of a transverse magnetic field on the growth of equiaxed grains during directional solidification

Effect of a High Axial Magnetic Field on the Structure of Directionally Solidified Al–Si Alloys

Effect of a Transverse Magnetic Field on Solidification Structure in Directionally Solidified Al-40 Wt% Cu Alloys

Effect of a High Magnetic Field on the Growth of Ternary Al-Cu-Ag Alloys During Directional Solidification

Investigation on Macrosegregation and Dendrite Morphology During Directional Solidification of Al-Cu Hypereutectic Alloys under A Strong Magnetic Field

EFFECT OF LONGITUDINAL MAGNETIC FIELD ON THE MICROSTRUCTURE OF DIRECTIONALLY SOLIDIFIED Al-40%Cu HYPEREUTECTIC ALLOY

Formation and Evolution of Stray Grains on Remelted Interface in the Seed Crystal During the Directional Solidification of Single-Crystal Superalloys Assisted by Vertical Static Magnetic Field

Microstructure and Crystallization Evolution of Directionally Solidified Al–Cu–Si Alloys With the Assistance of a Static Magnetic Field

Effects of DC Magnetic Field on Crystal Orientation and Mechanical Properties of Al-4.5Cu Alloy

Investigation on the Formation Mechanism of Irregular Dendrite During Directional Solidification of Al–Cu Alloys under a High Magnetic Field

Effect of a Weak Transverse Magnetic Field on the Morphology and Orientation of Directionally Solidified Al–Ni Alloys

EBSD Study of the Influence of a High Magnetic Field on the Microstructure and Orientation of the Al-Si Eutectic During Directional Solidification

The Evolution of Cube Texture in Directionally Solidified Fe-3.0 wt. % Si Alloy Assisted by a High Static Magnetic Field

Effect of a Transverse Magnetic Field on Solidification Structures in Unmodified and Sr-Modified Al-7wtpctSi Alloys During Directional Solidification

Effect of a Low Axial Magnetic Field on the Primary Al2Cu Phase Growth in a Directionally Solidified Al–Cu Hypereutectic Alloy