Abstract:Archaeological iron objects were excavated from the Nanhai I ship from the Southern Song Dynasty that sunk in the South China Sea. Most of these artifacts were severely corroded and fragmented. In order to understand their current corrosion state and guide their restoration and protection, optical microscopy, scanning electron microscopy, micro-laser Raman spectroscopy, infrared spectroscopy and X-ray diffraction were all selected for analysis. It was clear that the archaeological iron material was hypereutectic white iron with a carbon content of about 4.3-6.69%, and had experienced low-melt undercooling. There were many internal cracks formed by general corrosion that extended to the iron core, which tended to make the material unstable. At the interface between the iron and rust, there was a black dense layer enriched with chlorine, and a loose yellow outer layer. The dense layer was mainly composed of magnetite, akaganeite and maghemite, while the rust of the loose layer was composed of lepidocrocite, goethite, feroxyhite, maghemite and hematite. The major phases of all corrosion products were akaganeite and lepidocrocite. Numerous holes and cracks in the rust layer exhibited no barrier ability to the outside electrolyte, hence the iron core formed many redox electrochemical sites for general corrosion with the rust. Meanwhile, the dense rust located close to the iron core was broken locally by an enriched chlorine layer that was extremely detrimental to the stability of the archaeological iron. Using electrochemical impedance spectroscopy, it could be determined that the rust layers had no protective effect on the internal iron core under conditions of simulated seawater, and these rust layers even accelerated the corrosion. A mechanism for the rust growth as a result of laboratory testing was proposed to explain the entire corrosion process. In view of the desalination preservation treatment that had been applied for ten years, it was not recommended to maintain a single desalination operation. The archaeological rusted iron of the Nanhai I ship that was excavated from the marine environment should be properly stabilized and protected using corrosion inhibition and rust transformation for iron oxyhydroxides, since the rust structure and the internal iron core retain well together.

Rust Layers on Han Dynasty Coins with "Bright-Silver-Grey" Luster

Important Explorations on Surface Corrosion of the Copper Coins Sourced from the Qing Dynasty

Tarnishing and Pitting Corrosion Mechanism Revealed by Nanoparticles on the Gold Foil of Western Han Dynasty in Taiyuan, Shanxi, China Through a Multi-analytical Approach

Changes in pulmonary function test results after 1 year of therapy as predictors of survival in patients with idiopathic pulmonary fibrosis.

Chemical studies of Chinese coinage II: from Qin to Yuan (221 BCE–1368 CE)

Archaeometallurgical characteristics of coins in the Liao Dynasty (AD 907-1125): using metallographic microanalysis and SEM–EDS

Structure of Corrosion Layers on Archaeological Iron Artifacts From Nanhai I

Lead isotope and trace element analysis of the Wuzhu coins from Doujiaqiao hoard, Tianjin City, North China

“Inward Growth” Corrosion and Its Growth Mechanism in Ancient Chinese Bronzes

Understanding the Unique Corrosion Phenomenon of Sanxingdui Embrittled Gold Masks Using Scanning Electrochemical Cell Microscopy (SECCM): Intergranular Corrosion of Au-Ag-Pb Ternary Alloy

Early Stages of Metal Corrosion in Coastal Archaeological Sites: Effects of Chemical Composition in Silver and Copper Alloys

Corrosion Layers on Archaeological Cast Iron from Nanhai I

The corrosion mechanism of lead-glazed pottery in Han dynasty

Corrosion Mechanisms and Conservation Strategies for Marine Recovered Bronze Artifacts: Insights from the Nanhai No. 1 Shipwreck

Rust Conversion of Proanthocyanidins to Archaeological Steel: A Case Study of Lingzhao Xuan in the Forbidden City

Mechanism of corrosion behavior between Pb-rich phase and Cu-rich structure of high Sn–Pb bronze alloy in neutral salt spray environment

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Thrombotic thrombocytopenic purpura and its look-alikes: a single institution experience.

Study of Inhibition Performance of a Vapor Phase Inhibitor on Rusty Iron Coins

Non-destructive Phase Analysis of Song Dynasty Iron Coins by TOF Neutron Diffraction

Scanning Electrochemical Cell Microscopy: A Powerful Method to Study the Intergranular Corrosions of Archaeological Silver Artifacts