Abstract:Abstract Thousands of archaeological irons were excavated from the Nanhai I ship of the Southern Song Dynasty sunk in South China Sea, most of which were severely corroded and fragmented. To understand the current corrosion state and guide the restoration and protection, one piece of these iron objects was selected for analysis. Using optical microscope, scanning electron microscope, micro-laser Raman spectroscopy, infrared spectroscopy, and X-ray diffraction, it was clear that the archaeological iron was hypereutectic white iron with carbon content of about 4.3-6.69% and had experienced low melt undercooling. There were many internal cracks formed by general corrosion extending to the iron core which was a tendency of instability. At the interface between the iron and rust, there was a black dense layer enriched with chlorine and a loose outer layer in yellow. The dense layer was mainly composed of magnetite, akaganeite and maghemite, while the rust of the loose layer was about lepidocrocite, goethite, feroxyhite, maghemite and hematite. Besides, the major phases of all corrosion products were akaganeite and lepidocrocite. Numerous holes and cracks in the rust layer had no barrier ability to the outside electrolyte, so that the iron core formed many redox electrochemical sites to be general corrosion with the rust. Meanwhile, the dense rust close to the iron core was broken locally by enriched chlorine layer, which was extremely detrimental to the stability of the archaeological iron. By electrochemical impedance spectroscopy, it could be determined that the rust layers had no protective effect on the internal iron core indeed under the condition of simulating seawater, even accelerating corrosion. The mechanism of the rust growth was proposed from the shipwreck sinking to the laboratory testing to explain the entire corrosion process. Based on the concept of authenticity on the preservation, the archaeological rusted iron of the Nanhai I ship excavated from marine environment should be properly dechlorinated and necessarily stabilized, such as corrosion inhibition and reinforcement, for the rust structure and the internal iron core well-retained together.

Non-destructive Phase Analysis of Song Dynasty Iron Coins by TOF Neutron Diffraction

Archaeometallurgical investigation on the Han iron swords and knives unearthed from Xi'an, China

Developing a quantitative multimodal and multi-scale, fully non-destructive technique for the study of iron archaeological artefacts

Revealing the manufacturing and corrosion characteristics of Chinese archaeological metal arrows by non-destructive neutron techniques

Archaeometallurgical characteristics of coins in the Liao Dynasty (AD 907-1125): using metallographic microanalysis and SEM–EDS

Archaeometallurgical study of iron objects from a third century BC bone workshop in Xianyang, Shaanxi Province, China

Lead isotope and trace element analysis of the Wuzhu coins from Doujiaqiao hoard, Tianjin City, North China

Revisiting Trace Element Data and Metal Circulation Investigation of Western Zhou Bronzes

Chemical studies of Chinese coinage II: from Qin to Yuan (221 BCE–1368 CE)

Structural and compositional analysis of a casting mold sherd from ancient China

Structure of Corrosion Layers on Archaeological Iron Artifacts From Nanhai I

The Non-Destructive Analysis of Some Ancient Jade Artifacts Unearthed from Henan Province by a Variety of Optical Techniques

A two-way analytical investigation of ancient gold coins: Elemental and colorimetric description of precious materials

Corrosion Inhibition and Rust Conversion of Catechin on Archaeological Iron of Nanhai I

Nano-microcrystals revealed on Tang dynasty gilded bronze using advanced TEM-SEM and synchrotron methods

The beginning of iron corrosion - high-resolution visualization with 3D electron tomography

Quantitative measurement of cast metal relics by pulsed thermal imaging

The Early Cast Iron Processing Technology in Central China: Scientific Analysis on the Iron Artefacts from Ouerping Site, Shanxi Province, Ca.400bc-200Bc

Corrosion Behavior of Ancient White Cast Iron Artifacts from Marine Excavations at Atmospheric Condition

Non‐invasive surface analysis of ancient bronze arrowheads with scanning electron microscopy and X‐ray powder diffractometry

Development of a multi-isotopic (Pb, Fe, Cu) analytical protocol in gold matrices for ancient coin provenance studies