Abstract:Abstract Thousands of archaeological irons were excavated from the Nanhai I ship of the Southern Song Dynasty sunk in South China Sea, most of which were severely corroded and fragmented. To understand the current corrosion state and guide the restoration and protection, one piece of these iron objects was selected for analysis. Using optical microscope, scanning electron microscope, micro-laser Raman spectroscopy, infrared spectroscopy, and X-ray diffraction, it was clear that the archaeological iron was hypereutectic white iron with carbon content of about 4.3-6.69% and had experienced low melt undercooling. There were many internal cracks formed by general corrosion extending to the iron core which was a tendency of instability. At the interface between the iron and rust, there was a black dense layer enriched with chlorine and a loose outer layer in yellow. The dense layer was mainly composed of magnetite, akaganeite and maghemite, while the rust of the loose layer was about lepidocrocite, goethite, feroxyhite, maghemite and hematite. Besides, the major phases of all corrosion products were akaganeite and lepidocrocite. Numerous holes and cracks in the rust layer had no barrier ability to the outside electrolyte, so that the iron core formed many redox electrochemical sites to be general corrosion with the rust. Meanwhile, the dense rust close to the iron core was broken locally by enriched chlorine layer, which was extremely detrimental to the stability of the archaeological iron. By electrochemical impedance spectroscopy, it could be determined that the rust layers had no protective effect on the internal iron core indeed under the condition of simulating seawater, even accelerating corrosion. The mechanism of the rust growth was proposed from the shipwreck sinking to the laboratory testing to explain the entire corrosion process. Based on the concept of authenticity on the preservation, the archaeological rusted iron of the Nanhai I ship excavated from marine environment should be properly dechlorinated and necessarily stabilized, such as corrosion inhibition and reinforcement, for the rust structure and the internal iron core well-retained together.

Tarnishing and Pitting Corrosion Mechanism Revealed by Nanoparticles on the Gold Foil of Western Han Dynasty in Taiyuan, Shanxi, China Through a Multi-analytical Approach

Understanding the Unique Corrosion Phenomenon of Sanxingdui Embrittled Gold Masks Using Scanning Electrochemical Cell Microscopy (SECCM): Intergranular Corrosion of Au-Ag-Pb Ternary Alloy

Synergy Between Structure Characteristics and the Solution Chemistry in a Near/Non-Equilibrium Oxidative Etching of Penta-Twinned Palladium Nanorods

Nanoscale Kinetics of Asymmetrical Corrosion in Core-Shell Nanoparticles

Nano-microcrystals revealed on Tang dynasty gilded bronze using advanced TEM-SEM and synchrotron methods

Important Explorations on Surface Corrosion of the Copper Coins Sourced from the Qing Dynasty

Analysis of the manufacturing craft of the painted gold foils applied on the lacquerware of the Jin Yang Western Han Dynasty tomb in Taiyuan, Shanxi, China

Early Stages of Metal Corrosion in Coastal Archaeological Sites: Effects of Chemical Composition in Silver and Copper Alloys

Strain-Induced Corrosion Kinetics at Nanoscale Revealed in Liquid: Enabling Control of Corrosion Dynamics of Electrocatalysis

Dynamic Investigation of Cu50at%Au (001) Alloy Film Nano-oxidation by in Situ UHV TEM

“Inward Growth” Corrosion and Its Growth Mechanism in Ancient Chinese Bronzes

Natural corrosion-induced gold nanoparticles yield purple color of Alhambra palaces decoration

Scanning Electrochemical Cell Microscopy: A Powerful Method to Study the Intergranular Corrosions of Archaeological Silver Artifacts

[Using Raman spectrum analysis to research corrosive productions occurring in alloy of ancient bronze wares]

Structure of Corrosion Layers on Archaeological Iron Artifacts From Nanhai I

Surface chromium on Terracotta Army bronze weapons is neither an ancient anti-rust treatment nor the reason for their good preservation

Corrosion Mechanisms and Conservation Strategies for Marine Recovered Bronze Artifacts: Insights from the Nanhai No. 1 Shipwreck

Optimizing Metallographic Etchants for Ancient Gold and Silver Materials

Process and technical characteristics of traditional gilding technology on silver: experimental replication and analysis of silver gilded products

Microstructure and Chlorine Ion Corrosion Performance in Bronze Earring Relics

Unveiling Corrosion Pathways of Sn Nanocrystals through High-Resolution Liquid Cell Electron Microscopy