Giant Magnetoresistance Effect and Microstructure of Fe-Cu Granular Films

王长征,戎咏华,徐祖耀

DOI: https://doi.org/10.3969/j.issn.1008-1690.2004.04.005

2004-01-01

Abstract:The structures and properties of Fe 23Cu 77 granular films prepared with a magnetron controlled sputtering method were investigated through XRD, TEM, VSM and conventional four probes method. The results indicate that Fe granules with the sizes ranging from 1nm to 10nm distribute non-uniformly in the Cu matrix,and that the texture of Cu matrix exists in the granular films at room temperature. The measurement through VSM shows that granular films exhibit superparamagnetic nature at room temperature and that the magnetization curve fits with Langevin function. With the increase of annealing temperature, the GMR effect reaching the maximum value of-1.2% at room temperature decreases monotonously, which can attribute to that there exists an optimum surface-to-volume ratio of granules at room temperature in the granular films, enhancing the spin-dependent scattering and the GMR effect. Fitting GMR-(CM/MS) curve by using a nonlinear least-squars method,it is apparent that GMR effect has a proportional relation with (M/Ms)2 at low fields and deviate from proportional relation with (M/Ms)2 at high fields.