Abstract:Mg-1.5Y-1.2Zn-0.44Zr alloys were newly developed as degradable metallic biomaterials. A comprehensive investigation of the microstructure, mechanical properties, in vitro degradation assessments and in vitro cytotoxicity evaluations of the as-cast state, as-heat treated state and as-extruded state alloys was done. The microstructure observations show that the Mg-1.5Y-1.2Zn-0.44Zr alloys are mainly composed of the matrix α-Mg phases and the Mg12ZnY secondary phases (LPS structure). The hot extrusion method significantly refined the grains and eliminated the defects of both as-cast and heat treated alloys and thereby contributed to the better mechanical properties and biodegradation resistance. The values of tensile strength and tensile yield strength of the alloy in the as-extruded condition are about 236 and 178 MPa respectively, with an excellent elongation of 28%. Meanwhile, the value of compressive strength is about 471 MPa and the value of bending strength is about 501 MPa. The superior bending strength further demonstrates the excellent ductility of the hot extruded alloys. The results of immersion tests and electrochemical measurements in the SBF indicate that a protective film precipitated on the alloy's surface with the extension of degradation. The protective film contains Mg(OH)2 and hydroxyapatite (HA) which can reinforce osteoblast activity and promote good biocompatibility. No significant cytotoxicity towards L-929 cells was detected and the immersion extracts of alloy samples could enhance the cell proliferation with time in the cytotoxicity evaluations, implying that the Mg-1.5Y-1.2Zn-0.44Zr alloys have the potential to be used for biomedical applications.

Research Progress of Biomedical Degradable Mg-Zn Alloys

Research Progress in Biomedical Magnesium Alloys

Research Progress on the Alloying of Biodegradable Magnesium Alloys

Research status and future prospects of biodegradable Zn-Mg alloys

Application and development prospect of magnesium alloys as biomedical materials

Research Progress of Zn-Based Alloys as Biodegradable Materials

Research Progress in Degradation Behavior of Biodegradable Medical Mg-based Alloys in Vivo and in Vitro

Research Progress on Corrosion Behaviors and Improvement Methods of Medical Degradable Mg−Based Alloys

Degradable magnesium-based alloys for biomedical applications: The role of critical alloying elements

Systems, Properties, Surface Modification and Applications of Biodegradable Magnesium-Based Alloys: A Review

Research Progress of Biodegradable Magnesium-Based Biomedical Materials: A Review

Research Progress on Biocompatibility Evaluation of Biomedical Degradable Zinc Alloys

Research on an Mg-Zn alloy as a degradable biomaterial.

Research Progress in Biodegradable Metallic Materials for Medical Application

Antibacterial Properties, Hemolysis and Biocompatibility of Biodegradable Medical Magnesium Alloys

Microstructure, Mechanical Properties, in Vitro Degradation and Cytotoxicity Evaluations of Mg–1.5Y–1.2Zn–0.44Zr Alloys for Biodegradable Metallic Implants

The Latest Research Progress in Biodegradable Magnesium Alloys

Recent advances on the development of magnesium alloys for biodegradable implants

A review on magnesium alloys for biomedical applications

Advances on biodegradable zinc-silver-based alloys for biomedical applications

Research on Biodegradable Mg-Zn-Gd Alloys for Potential Orthopedic Implants: in Vitro and in Vivo Evaluations.