Effect of Current Density on Zn-Ni-Mn Alloy Coating Prepared by Pulse Electroplating

Xinyue WANG,Haili YANG,Zhitong ZHANG,Haipeng LIU,Qingbo MENG,Yungang LI
DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.14.048
2017-01-01
Abstract:Zn-Ni-Mn alloy coatings were prepared on Q235 steel substrate by pulse electroplating. The effects of current density on the surface morphology, composition, electrodeposition rate and corrosion resistance of Zn-Ni-Mn alloy coating were studied. The results show that with current density increasing, the electrodeposition rate increases firstly and then decreases. Mn content in the alloy coating increases while zinc and Mn contents decrease. The corrosion resistance of the alloy coating increases firstly and then decreases with the increase of current density. The coating obtained at current density of 3. 0 A·dm-2 is smooth and compact, and has the best corrosion resistance. The corrosion resistance of Zn-Ni-Mn alloy coating in 3. 5% NaCl solution is better than in 5. 0% NaOH solution.
What problem does this paper attempt to address?