Investigation of Al-matrix Composites Reinforced by TiC Particulates Synthesized from Melt and Corresponding Properties

Mousheng SONG,Jie ZHANG,Yong LI,Ying WANG,Dongfang ZHANG

DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.20.031

2017-01-01

Abstract:TiC particulates were in-situ reactively synthesized from the high-temperature Al melt and thus the Al-matrix composites with the different mass fraction TiC reinforced phase were prepared. It is found that, the in-situ formed TiC phase binds tightly with the matrix, and can refine the matrix microstructure availably. With the TiC content in the matrix increasing, the composites' densification decreases, but the hardness rises and achieves the maximum at 10wt％ TiC content. The friction testing shows that, the wear loss ratio of composites reduces with the TiC reinforced particulates increasing. Under 10 N and 25 N loading after suffering from 30 m worn distance, the worn weight loss ratios of composites are just 0.45％ and 0.67％, respectively, which means it has the excellent wear resistance property. After friction, a large number of clear and parallel "plough" trace appears on the surface of the composites, and the friction mechanism is mainly fatigue abrasion mode.