Effect of Short-Aging Treatment on Microstructure and Micro-hardness of HR3C Alloy

侯本睿,赵新宝,杜双明,党莹樱,谷月峰

DOI: https://doi.org/10.14158/j.cnki.1001-3814.2016.18.066

2016-01-01

Abstract:Effects of short-aging treatment on microstructure and micro-hardness of HR3C alloy were investigated.The results show that grain size of the alloy after aging at 600-750 ℃ for 1h or 5 h is smaller than that of the alloy after solution treatment at 1200 ℃ for 30 min.With aging temperature increasing,the grain size decreases slightly,and after aging for 5 h,the decrease of the grain size is morre obvious.During the short-term aging process,M23C6 carbides are separated out on the grain boundary of HR3(C.With the incrrease of the heat preservation temperature and holding time,the amount of carbides increases slightly,and the size is almost no change.Meanwhile,nano Z phase nucleates and grows up in the crystal.Compared with the solid solution,the micro-hardness of the alloy increases after short-aging treatment.Extending the holding time,the hardness of the alloy is basically stable.