Effect of Heat Treatment on the Microstructure and Properties of Alloy K403

Shuaifeng Jiang,Zhigang Yang,Shaoao Shen

DOI: https://doi.org/10.3321/j.issn:1002-185X.2008.05.027

2008-01-01

Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering

Abstract:The microstructure features, tensile and hardness properties of K403 superalloy at as-cast, as-solution and as-aged conditions were investigated using optical microscopy and scanning electron microscopy in detail. The results show that the γ’ precipitates with two sizes were obtained after uncompleted solid solution at 1140 ℃ and 1180 ℃ for 4 h. Uniform cubical γ’ precipitates about 0.2 μm in size were obtained after completed solid-solution at 1210 ℃ for 4 h and air cooling. The tensile properties and room temperature hardness of the alloy are obviously improved after aging. Compared with other heat treatments, the alloy yields the best tensile properties and hardness after treatments of 1190 ℃, 4 h,air cooling + 940 ℃, 16 h, and air cooling. When aging at 980 ℃ for 16 h, the γ’ phase became coarser (0.3~0.6 μm), resulting in the decrease of properties and hardness.