Abstract:This study investigates the substitution of cerium (Ce) with mischmetal (MM) in cast Al-MM alloys, focusing on microstructure, hardness, tensile and compression properties, creep resistance, and coarsening resistance. Al-MM alloys with various MM compositions (Ce, Ce-50La, Ce-33La, and Ce-27La-19Nd, weight percent) exhibit near-eutectic and hyper-eutectic microstructures for Al-9MM and Al-12MM compositions, respectively, with similar as-cast hardness (~525 MPa). All Al-9MM alloys show tensile yield stress ~55 MPa, ultimate tensile strength ~130 MPa, and fracture strain ~8%.The microstructural and mechanical properties consistency demonstrates the flexibility of MM compositions in Al-MM alloys. Al-9MM exhibits excellent coarsening resistance, with minimal hardness reduction when exposed to 300 and 350 C for up to 11 weeks, and a modest ~15% hardness reduction at 400 C for 8 weeks, outperforming eutectic Al-12.6Si and Al-6.4Ni alloys. Additionally, Al-9MM shows higher creep resistance at 300 C compared to most precipitate-strengthened Al-Sc-Zr and solid-solution-strengthened Al-Mg/Mn alloys, but is outperformed by eutectic-strengthened Al-6.4Ni and Al-10Ce-5Ni alloys.The effect of casting cooling rate is investigated through wedge casting: Al-9Ce transitions from hypo- to hyper-eutectic as cooling rates decrease, while Al-12Ce consistently shows hyper-eutectic microstructures. Al11Ce3 lamellae become finer and more closely spaced with increasing cooling rates. Al-9Ce maintains steady hardness at high to moderate cooling rates but shows reduced hardness at lower rates, whereas Al-12Ce shows no change in hardness.With a 15% reduction in energy consumption and CO2 emissions, Al-Ce alloys where Ce is replaced with MM offer comparable mechanical properties and enhanced environmental benefits, highlighting the potential of MM as a sustainable alternative.

Effect of Cerium-rich Mischmetal on Microstructures of As-cast A356 Alloy

Effect of Mischmetal Modification Treatment on the Microstructure, Tensile Properties, and Fracture Behavior of Al-7.0%Si-0.3%Mg Foundry Aluminum Alloys

Effect of Cerium on Microstructure, Texture and Properties of Ultrahigh-Purity Copper

Effect of Mass Fraction of Mischmetal Addition on Microstructures of A356 Alloy

Effect of minor cerium additions on microstructure and mechanical properties of cast Al – Cu – Mg – Ag alloy

Effects of Mischmetal Composition and Cooling Rates on the Microstructure and Mechanical Properties of Al-(Ce, La, Nd) Eutectic Alloys

Influence of Cerium and Mischmetal on the Hardness and Brightness of AlMgSi Alloys

Effect of Rare Earth Elements Erbium and Europium Addition on Microstructure and Mechanical Properties of A356 (Al–7Si–0.3Mg) Alloy

Effect of Cerium on Microstructures and Mechanical Properties of Az61 Wrought Magnesium Alloy

Effect of Mischmetal Addition on Microstructure and Mechanical Properties of As-Cast and As-Rolled Mg–Sn–Ca Alloys

Effect of Cerium Addition on Microstructure and Mechanical Properties of As-Cast High Grade Knives Steel

Effect of Cerium on the As-Cast Microstructure and Tensile Ductility of the Twin-Roll Casting Fe–6.5 Wt% Si Alloy

Effects of Mg, Ce and Cu Content on Microstructure of 2D70 Aluminum Alloy

Influence of cerium treatment on inclusion modification and as-cast microstructure of high-strength low-alloy steel

Effect of Ce Content on the Microstructure of Semisolid Mg-10Al Alloy

Effect of the addition of cerium on the microstructure evolution and thermal expansion properties of cast Al-Cu-Fe alloy

The Effect of Grain Refinement and Precipitation Strengthening Induced by Sc or Er Alloying on the Mechanical Properties of Cast Al-Li-Cu-Mg Alloys at Elevated Temperatures

Effect of Fe, Mn, Ce on the Microstructure and Mechanical Properties of Al-Mg and Al-Mg-Si Die Casting Alloys

Effect of Ce Content on the Microstructure and Mechanical Properties of Squeeze-Cast Al–5Mg-2.2Si-0.6Mn Alloys

Effect of cerium on the primary carbides and inclusions in electroslag remelted M35 high speed steel

Effect of Partially Substituting Ca with Mischmetal on the Microstructure and Mechanical Properties of Extruded Mg–Al–Ca–Mn-Based Alloys