Abstract:The microstructural characteristics and morphological attributes of the target material, along with its intrinsic properties, can significantly influence the performance of the resultant film. Currently, commercially available nickel-vanadium targets employed in the industry have not been subjected to investigations aimed at controlling grain size and grain orientation. This study examines the effects of unidirectional rolling at room temperature, combined with substantial deformation, on the alterations in microstructure, texture evolution, and mechanical properties of the NiV7 alloy. The process of severe plastic cold rolling leads to a continuous elongation and refinement of the grains. The changes in microstructure and texture of the cold-rolled sheets were analyzed using electron backscatter diffraction (EBSD) technology. At an 80% reduction, a significant number of sub-grains are observed, which transform into deformed grains as the reduction reaches 95%. With a thickness reduction of 96.6%, the average grain size is approximately 1.10μm. Further increases in reduction do not lead to significant alterations in the grain structure; instead, the grain orientation progressively becomes more uniform with higher levels of deformation. The combination of substantial deformation and lower rolling rates results in an increased number of high-angle grain boundaries. The alloy displays various textures throughout the rolling process, including S-type, copper-type, brass-type, fiber, and cubic textures. Notably, the prevalence of S-type and fiber textures diminishes as the degree of deformation increases, while the cubic texture becomes increasingly prominent. Upon achieving a reduction of 95%, the cubic texture emerges as the dominant texture. A transmission electron microscope (TEM) was utilized to examine the extensive array of dislocations, dislocation cells, dislocation walls, and shear bands generated during the cold rolling process. At a deformation level of 96.6%, the ultimate tensile strength of the alloy demonstrates a significant enhancement, attributed to mechanisms of dislocation strengthening and grain strengthening, reaching a value of 1231±20 MPa, accompanied by a post-fracture elongation of approximately 2%. The ultimate tensile strength exhibited an increase of 781±20 MPa compared to the sample prior to the rolling process; however, there was a notable reduction in plasticity.

Effect of Carbides on Crack Behavior Within Rolls under Cold Rolling Condition

Investigation on wear behaviors of high-vanadium high-speed steel compared with high-chromium cast iron under rolling contact condition

Rolling/sliding Wear Property and Failure Behavior of High-vanadium High-speed Steel for Rolls

Effects of Carbides Distribution in Matrix on Thermal Fatigue and Wear Properties of High Speed Steel Rolls

Microstructure and Wear Properties of Fe-V-Cr-Mo Alloy Rolls

Comparative Investigation to Rolling Wear Properties Between High-Vanadium High-Speed Steel and High-Chromium Cast Iron

Microstructural effects on central crack formation in hot cross-wedge-rolled high-strength steel parts

Effects of Carbon Content and Sliding Ratio on Wear Behavior of High-Vanadium High-Speed Steel (hvhss) under High-Stress Rolling Sliding Contact

Effect of Carbides on Thermos-Plastic and Crack Initiation and Expansion of High-Carbon Chromium-Bearing Steel Castings

Microstructure Evolution and Micro-Mechanical Behavior of Secondary Carbides at Grain Boundary in a Fe–Cr–W–Mo–V–C Alloy

Failure Analysis on Vertical Cracking of Medium Carbon Bainitic Steel Backup Roll

Severe plastic cold rolling effects in Nickel-Vanadium alloy: Microstructure, texture evolution and mechanical properties

A Study on CrMo WVNb White Cast Iron Roll Manufactured with Centrifugal Casting Process

Study on High Chromium Cast Iron Fracture Grinding Roll

Insight into the impact of microstructure on crack initiation/propagation behavior in carbide-free bainitic steel during tensile deformation

Effect of Hot-Rolling Deformation on Microstructure and Sliding Wear of High-Chromium Cast Iron

Vertical Short Crack Initiation in Medium Carbon Bainitic Steel Under Mild Tractive Rolling Contact

Effect of particle size and high-energy ball milling time on microstructure and mechanical properties of WC-10Co cemented carbides with plate-like WC grains

Effect of Matrix Microstructure on Wear Behaviors of High-speed Steel with High Vanadium Content under Dry Sliding Condition

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Ratcheting short crack behavior in medium carbon bainitic back-up roll steel under mild tractive rolling contact