Low temperature hybrid 3D printing of hierarchically porous bone tissue engineering scaffolds with in situ delivery of osteogenic peptide and mesenchymal stem cells
Jiahui Lai,Chong Wang,Jia Liu,Shangsi Chen,Chaoyu Liu,Xiangxuan Huang,Jing Wu,Yue Pan,Yuancai Xie,Min Wang
DOI: https://doi.org/10.1088/1758-5090/ac84b0
2022-07-29
Biofabrication
Abstract:Comparing to other conventional fabrication techniques, 3D printing is advantageous in producing bone tissue engineering scaffolds with customized shape, tailored pore size/porosity, required mechanical properties and even desirable biomolecule delivery capability. However, towards scaffolds with a large volume, it is highly difficult to enable seed cells to migrate to the central region of the scaffolds, resulting in an inhomogeneous cell distribution, and hence lowering the bone forming ability. To address this problem, in this investigation, cell-laden bone tissue engineering scaffolds consisting of osteogenic peptide loaded β-tricalcium phosphate/poly(lactic-co-glycolic acid) (OP/TCP/PLGA) nanocomposite scaffolds and rat bone marrow derived mesenchymal stem cells (rBMSCs)-laden Gelatin/GelMA hydrogel fillers were produced through a "dual-nozzle" cryogenic hybrid 3D printing. The cell-laden scaffolds exhibited a bi-phasic structure and were mechanically similar to human cancellous bone. OP can be released from the hybrid scaffolds in a sustained manner. rBMSCs laden in the hydrogel patterns exhibited a high viability during and after cryogenic hybrid 3D printing process and can be further released from the hydrogel struts and achieve cell anchorage on the surface of adjacent OTP struts. The OP released from OTP struts enhanced rBMSCs proliferation. Comparing to rBMSC-laden hybrid scaffolds without OP incorporation, the rBMSC-laden hybrid scaffolds incorporated with OP significantly up-regulated the osteogenic differentiation of rBMSCs, by showing a higher level of alkaline phosphatase (ALP) expression and calcium deposition. This "proof-ofconcept" study provided a facile method to form cell-laden bone tissue engineering scaffolds with not only required mechanical strength, biomimetic structure and prolonged biomolecule release but also excellent cell delivery capability with uniform cell distribution.
engineering, biomedical,materials science, biomaterials