Abstract:In order to solve the problem of shield hobbing cutter failure due to bias wear and chipping during tunnel boring, TiC-WC/Ni60 coating was prepared on the surface of H13 steel to improve the wear resistance of shield hobbing cutter. In this paper, four kinds of WC-TiC/Ni60 composite coatings with different content ratios of 5 wt% TiC+25 wt% WC, 10 wt% TiC+20 wt% WC, 15 wt% TiC+15 wt% WC and 20 wt% TiC+10 wt% WC were prepared on the surface of H13 steel by using the coaxial powder-feeding laser cladding equipment. The micromorphology, phase, hardness and friction and wear properties were fully studied. The results show that cross-sectional organization of the fused cladding layer mainly consists of columnar crystals, cytocrystals and equiaxial crystals; the hard phases in the fused cladding layer mainly consist of TiWC 2 , Cr 4 Ni 5 W, and Cr 3 C 2 , and so on; The microhardness of the cross-section of the fused cladding layer shows a trend of decreasing at first, then increasing and finally decreasing, and the highest hardness of the fused cladding layer occurs at the subsurface of the fused cladding layer; the friction coefficient of the fused cladding layer shows a trend of decreasing first and then increasing; the wear volume of the fused cladding layer is significantly lower than that of the substrate, and the wear volume of the 15 wt% TiC coating is the smallest of 1.313 mm 3 , which is 86.9 % lower than that of the substrate; the wear mechanism of the substrate is mainly abrasive wear and adhesive wear, and the wear mechanism of the fused cladding layer is mainly brittle spalling, abrasive wear and oxidative wear. The analysis of the experimental results shows that the surface properties of the coating are best when both TiC and WC contents are 15 wt%.

Dry-sliding tribological properties of laminated WC/TiC ceramic cutting tool material sliding against 316 L austenitic stainless steel

Tribological behavior of modified polyetheretherketone composites in sliding against stainless steel under water lubrication

Wear Behaviour and Microstructural Changes of SiCw-Al Composite under Unlubricated Sliding Friction

Wear Behavior of Al 2 O 3 -Ticn Composite Ceramic Sliding on Stainless Steel

Wear mechanisms of Ti(C, N) ceramic in sliding contact with stainless steel

Tribological behaviour of TiB2-HfC ceramic tool material under dry sliding condition

Tribological Characteristics of Si3N4 Ceramic Sliding on Stainless Steel

Tribological Behavior of TiC Particles Reinforced 316Lss Composite Fabricated Using Selective Laser Melting

Friction and Wear of Si3N4 Ceramic/stainless Steel Sliding Contacts in Dry and Lubricated Conditions

Wear Behavior of Si3N4 Ceramic Cutting Tool Material Against Stainless Steel in Dry and Water-Lubricated Conditions

Friction and wear behaviors of Al 2 O 3 /TiC micro-nano-composite ceramic sliding against metals and hard materials

Preparation of Ultra-Fine ATC Ceramics and Analysis of Its Dry-Sliding Wear Behavior

Tribological performance of DLC-coated ceramics against cemented carbide under dry sliding conditions

Study of the Fatigue Wear Behaviors of a Tungsten Carbide Diamond-Like Carbon Coating on 316L Stainless Steel

Tribological Properties of Additive Manufactured Ti6Al4V Against Cemented Carbide under Dry Sliding Conditions

STUDY ON THE WEAR PERFORMANCES OF CERAMIC TOOLS FOR MACHINING 304 STAINLESS STEEL

Microstructure and tribological properties of laser cladded TiC reinforced WC-10Co4Cr coatings at 500 °C

Tribological Properties of Carbon-Fibre-reinforced Plastic Against Tungsten Carbide under Dry Condition

Friction and wear characteristics of plasma-sprayed WC coatings in dliding against GCr15 steel

Friction and wear of titanium alloys sliding against metal, polymer, and ceramic counterfaces

Study on the friction and wear performance of laser cladding WC-TiC/Ni60 coating on the working face of shield bobbing cutter