Cobalt-Doped NiS 2 Micro/Nanostructures with Complete Solid Solubility as High-Performance Cathode Materials for Actual High-Specific-Energy Thermal Batteries
Hao Guo,Licheng Tang,Qianqiu Tian,Ying Chu,Bin Shi,Xucai Yin,Hua Huo,Xiaopeng Han,Chengxiang Yang,Chu Wang,Kangkang Tang,Chang Wang,Xiaohong Zhang,Jianyong Wang,Long Kong,Zhouguang Lu
DOI: https://doi.org/10.1021/acsami.0c13396
2020-10-29
Abstract:Transition-metal sulfides are key cathode materials for thermal batteries used in military applications. However, it is still a big challenge to prepare sulfides with good electronic conductivity and thermal stability. Herein, we rapidly synthesized a Co-doped NiS<sub>2</sub> micro/nanostructure using a hydrothermal method. We found that the specific capacity of the Ni<sub>1–<i>x</i></sub>Co<i><sub>x</sub></i>S<sub>2</sub> micro/nanostructure increases with the amount of Co doping. Under a current density of 100 mA cm<sup>–2</sup>, the specific capacity of Ni<sub>0.5</sub>Co<sub>0.5</sub>S<sub>2</sub> was about 1565.2 As g<sup>–1</sup> (434.8 mAh g<sup>–1</sup>) with a cutoff voltage of 1.5 V. Owing to the small polarization impedance (5 mΩ), the pulse voltage reaches about 1.74 V under a pulse current of 2.5 A cm<sup>–2</sup>, 30 ms. Additionally, the discharge mechanism was proposed by analyzing the discharge product according to the anionic redox chemistry. Furthermore, a 3.9 kg full thermal battery is assembled based on the synthesized Ni<sub>0.5</sub>Co<sub>0.5</sub>S<sub>2</sub> cathode materials. Notably, the full thermal battery discharges at a current density of 100 mA cm<sup>–2</sup>, with an operating time of about 4000 s, enabling a high specific energy density of around 142.5 Wh kg<sup>–1</sup>. In summary, this work presents an effective cathode material for thermal battery with high specific energy and long operating life.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c13396?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c13396</a>.XRD patterns of synthetic products obtained at 180 or 200 °C at different heating times; XRD patterns with the corresponding Rietveld refinement of Ni<sub>1–<i>x</i></sub>Co<i><sub>x</sub></i>S<sub>2</sub> (<i>x</i> = 0.1–0.4), NiS, and CoS<sub>2</sub>; EDS patterns and the corresponding selected area of the as-prepared Ni<sub>1–<i>x</i></sub>Co<i><sub>x</sub></i>S<sub>2</sub> (<i>x</i> = 0.1–0.5); HRTEM image of Ni<sub>0.5</sub>Co<sub>0.5</sub>S<sub>2</sub>; and electrochemical performance of NiS and CoS<sub>2</sub> (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c13396/suppl_file/am0c13396_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology