Failure Mechanism and Residual Stress Analysis of Crystal Materials for the Thermal Battery

Wei Su,Ming Chen,Zhizhe Wang,Butian Zhong,Zhenhua Nie
DOI: https://doi.org/10.3390/cryst14020198
IF: 2.7
2024-02-20
Crystals
Abstract:This paper investigates the thermal battery as a research topic. We conducted an in−depth analysis of various thermal battery aspects, such as the cathode material CoS2 and electrolyte material morphology, crystal type, and interface state changes before and after service. The aim was to explore the core reaction and main failure mechanisms of the thermal battery. Prior to the reaction, the thermal battery cathode and electrolyte material consisted of pure−phase CoS2 and a composition of MgO−LiF/LiBr/LiCl. After service, the cathode and electrolyte of the single thermal battery exhibited significant morphological alterations caused by the presence of a molten state. The cathode transformed from CoS2 to Co3S4 and Co9S8 together with the presence of a marginal quantity of Co monomers visible throughout the discharge process, which was confirmed by means of XRD and XPS analyses. After the reaction, the electrolyte material was primarily made up of LiF, LiBr, and LiCl while the crystal components remained largely unaltered, albeit with apparent morphological variations. As was deduced from the thermodynamic analysis, the cathode material's decomposition temperature stood at 655 °C, exceeding the working temperature of the thermal battery (500 °C) by a considerable margin, which is indicative of outstanding thermal durability within the thermal battery's operational temperature range. Furthermore, the discharge reaction of the positive electrode was incomplete, resulting in reduced CoS2 residue in the thermal battery monomer after service. The reaction yielded a combination of Co3S4, Co9S8, and small amounts of Co monomers, indicating possible inconsistencies in the phase composition of the pole piece during the reaction process. In this study, we examine the distribution of residual stress in the thermal battery under various operating conditions. The simulation results indicate that exposure to a 70 °C environment for 2 h causes the maximum residual stress of the battery, which had an initial temperature of 25 °C, to reach 0.26 GPa. The thermal battery subjected to an initial temperature of 25 °C exhibited a maximum residual stress of 0.42 GPa subsequent to a 2−hour exposure to a temperature of −50 °C.
materials science, multidisciplinary,crystallography
What problem does this paper attempt to address?
The problems that this paper attempts to solve are the core reaction mechanism and the main failure mechanism existing in the operation process of thermal batteries. Specifically, the research aims to reveal the key reaction processes inside the thermal battery and the causes of performance degradation by in - depth analysis of the morphology, crystal type and interface state changes of the positive electrode materials (such as CoS₂) and electrolyte materials of the thermal battery before and after use. ### Research Background and Problem Description 1. **Application Background of Thermal Batteries**: - Thermal batteries are reserve batteries that are activated and used in high - temperature environments and are widely used in the defense field, such as in the guidance systems and electronic devices of weapon systems like missiles and torpedoes. - The electrolyte of a thermal battery is a solid non - conductive inorganic halide salt at room temperature, such as LiCl - KCl eutectic salt, but it melts after being heated, enabling the battery to discharge rapidly. 2. **Research Objectives**: - **Explore the Core Reaction Mechanism**: Understand the chemical reactions occurring inside by analyzing the changes of the positive electrode material CoS₂ and the electrolyte material of the thermal battery before and after use. - **Reveal the Main Failure Mechanism**: Study the residual stress distribution of thermal batteries under different operating conditions and the impact of these stresses on battery performance. 3. **Specific Problems**: - **Changes in Positive Electrode Materials**: Study the decomposition behavior of CoS₂ in a high - temperature environment and its products (such as Co₃S₄, Co₉S₈ and a small amount of elemental Co), and verify them by means such as XRD and XPS. - **Stability of Electrolyte Materials**: Analyze the morphological changes of electrolyte materials (such as LiF, LiBr, LiCl) at high temperatures and their impact on battery performance. - **Residual Stress Analysis**: Study the residual stress distribution of thermal batteries in different temperature environments by finite - element simulation and evaluate its impact on battery life and performance. ### Main Research Contents - **Material Characterization**: Use techniques such as SEM, XRD, EDX and XPS to conduct detailed morphological, compositional and crystal - structure analyses of the positive, negative and electrolyte materials of thermal batteries. - **Thermodynamic Analysis**: Determine the decomposition temperature of the positive electrode material CoS₂ by thermogravimetric analysis (TGA) and evaluate its thermal stability within the working temperature range. - **Residual Stress Simulation**: Use the finite - element analysis method to simulate the residual stress distribution of thermal batteries under different operating conditions and explore the impact of temperature changes on the internal stress of the battery. Through these studies, the author hopes to provide a theoretical basis for the design and optimization of thermal batteries and improve their reliability and performance in high - requirement applications.