Abstract:In this paper, a study concerning self-breakdown voltage characteristics, electrode erosion, and degradation of the insulator, of a two-electrode spark-gap switch has been presented based on experiments. A 6 mu F pulse capacitor and a DC high voltage source (set at -40 kV) were utilized to achieve similar to 0.1 pulses per second repetitive arc discharge between two fixed Cu-W (Cu30/W70) alloy electrodes in the 1.2 L airtight chamber of the switch. With average transfer charge of 2.2 C per shot, this switch was tested for 5800 shots altogether. The results demonstrated the electrode erosion rate of the cathode was 6.3434x10(-6) cm(3)/C whereas that of anode was 5.4691x10(-6) cm(3)/C. Besides, by analyzing electrode surfaces' morphology and PTFE insulator surfaces' compositions after 5800 shots with the help of a scanning electron microscope, a dynamic 3D aspheric metrology instrument, an X-ray photoelectron spectrometer, a metallographic microscope, and a Mettler-Toledo analytical balance, some evidence of physical processes and chemical reactions between plasma channel, electrode materials, and insulation materials could be observed. Moreover, the chamber was opened and inspected for 10 times during the whole procedure, thus providing an overall description of the variation of the switch. It should also be pointed out that owing to complex mechanisms during the aging process, the self-breakdown voltage followed a mixed Normal distribution other than any other simple distributions.

Experimental Investigation of Electrical Performance of AgCdO Contact Material under Switching Capacitive Load Conditions

Study on Switching Characteristics and Associated Degradation Mechanism of Contact Material under Capacitive Load

Preliminary study on switching characteristics of silver tin oxide type contacts for capacitive load

An Experimental Investigation of Dynamic Welding Mechanism of Contacts Used in Low Current Switching Devices

Research on the Rolling and Sliding Behavior of Making Contact and Associated Welding Mechanism for Low-Current Switching Devices

Effect Of Electrical Load On Contact Welding Failure Of Silver Tin Oxide Material Used In Dc Electromechanical Relays

In Situ Observation and Understanding of the Arc Erosion Behavior of Electrical Contact Materials

Investigation of Switching Characteristics of Contact Materials for Inductive Load

Experimental Study On Arcing Process And Contact Erosion Under Transverse Magnetic Field

Study on the Mechanism of Arc Transition from Metallic Phase to Gaseous Phase

The Contact Resistance And Arc Erosion Behavior Of Separable Cp-Nb-Cr/Cu-Cd Electrical Contact Material

In Situ Interface Characterization of Arcing Electrode Materials and Evolution in Electrical Endurance Experiments

Influence of Operation Numbers on Arc Erosion of Ag/CdO Electrical Contact Materials

Experimental Study of Electrode Erosion and Aging Process of a Specially Designed Gas Switch under Repetitive Arc Discharge

A New Test Equipment for Measuring Electrical Contact Behaviors of Contact Materials and Experimental Study

Progress in Cu-based Contact Materials of Low Voltage Apparatus

Experimental Investigation on the Hot Switching Capability and Associated Failure Mechanism of Electrical Connectors

Contact Welding Strength Measurement for Metal Electrode Materials Conducting Inrush Electrical Current.

Experimental Investigation of Alternating Current Arc Behavior and Associated Contact Welding Failure for General-purpose Relay

Thermal and arc erosion behavior of CuCr contact material based on large plastic deformation treatment

Experimental Investigation of Contact Welding Characteristics of Electromechanical Relays