Abstract:This paper proposes an economical thermal cycle of the production of ceramic articles from submicronic powders of aluminum oxide, titanium oxide, and manganese oxide. The implementation of a given cycle involves the introduction of a special aluminophosphate bond into the charge in order to reduce the temperature of firing. The optimal composition of the material for a foam-ceramic filter with the highest physical and mechanical properties has been determined; the optimal method for preparing the original charge and the baking mode have been selected. According to the results of tests under industrial conditions, the manufactured alumina filters became a decent alternative to known analogs used in aluminum metallurgy for the purification of liquid metal. The application and rational dosage of titanium dioxides, manganese, and aluminum aluminophosphate in porous ceramic compositions on an alumina base have made it possible to significantly reduce the time and, consequently, improve the productivity, of firing. The results obtained were evaluated by the level of maximum temperature in the cycle of heat treatment according to known technologies. Compared to those technologies, the developed technology ensures the growth of firing productivity when implementing the proposed solution by about 220 %. It was found that the high true density of ceramic powder requires large dispersion as the relatively large powder particles are significantly worse retained in foam films and settle. At medium (intermediate) temperatures, a large weight loss occurs at a heating rate of 10 °C/h. In this case, the decomposition progress changes in proportion to the heating speed. Changing the heating speed with temperature is the most effective technique for deparaffinization in the air. The heating time from the ambient temperature to 200 °C significantly decreases. At a certain temperature, prior to the thermal decomposition, the bond would transfer from a strongly viscous state to a liquid state

Optimization of Preparation Procedure for High Temperature Exhaust Gas Filtering Ceramics by Orthogonal Test

Preparation and Properties of Filtering Ceramics for High Temperature Exhaust Gas

Impact of the Mineral Composition and Sintering Temperature on the Synthesis of Anorthite Ceramics

PREPARATION AND CHARACTERIZATION OF SiC POROUS CERAMICS SUPPORT

Preparation of Porous Ceramic Support with Inorganic Filtration Membrane

Study on Environment-Friendly Porous Ceramic Material

Study on Porous Mullite Ceramic Material Based on Orthogonal Experimental Method

Formation, Conversion and Elimination of Intermediate Spinel Phase in MgO/kaolin Mixture Firing for Cordierite

Process optimization of porous Al 2 O 3 filter via layered extrusion forming

Preparation of Anorthite/Mullite In Situ and Phase Transformation in Porcelain

Preparation and characteristics of porous anorthite ceramics with high porosity and high‐temperature strength

Process Parameters Appraisal of Fabricating Ceramic Parts Based on Stereolithography Using the Taguchi Method

Preparation of Porous Wollastonite Ceramics for Filtration

Production of porous ceramic from clinoptilolite incorporating aluminum powder

Hot-pressing of BeO Ceramics and Its Thermal Conductivity and Flexural Strength

Low‐temperature preparation of high‐performance porous ceramics composed of anorthite platelets

Examination of patterns in obtaining porous structures from submicron aluminum oxide powder and its mixtures

Study on the Effect of Binders on the Properties of Mullite Porous Ceramics for Flue Gas Filtration

Optimization of hydrothermal autoclaving parameters for the synthesis of porous ceramics from porcelain tile polishing residue

Response surface optimization and finite element simulation to prepare microporous carbon refractories via cold isostatic pressing

Optimization of 3D Printing Parameters for Alumina Ceramic Based on the Orthogonal Test