Study on SUS304 Ultra-thin Sheet withContinuous Fiber Laser Welding

Xuekai Zhou,Gaoyang Mi,Fei Yan,Shuo Li,Xiyuan Hu,Chunming Wang
DOI: https://doi.org/10.14128/j.cnki.al.20173704.521
2017-01-01
Applied laser
Abstract:Processed Continuous-Fiber-laser lap welding to 0.3 mm thickness of SUS304 using fiber laser with 1 080 nm.The result shows that the lapped sheets can be welded well using 600 W power with speed of 6 m/min,ltra-thin sheet welding speed can reach more than 10 m/min without hump and othen defects.Further study have carried out about microstructure.When the heat input is low,thus cooling rate is high,it turn out to be full Austenite.When the heat input behigher,weld seam will have a bit of-Ferrite,and the microstructure shows plaque morphology without obvious columnar grains,in other words,columnar grains are replaced by these plaque structure.It grows from weld seam edge to center and converges in the center.There are not equiaxial grains in the center of weld seam.The hardness of weld seam is lower than HAZ,in which the hardness is lower than base metal.When proceeding mechanical tensile,fracture shows a ductile fracture,and tensile strength is 620 MPa.
What problem does this paper attempt to address?