Abstract:Although ethylene oxide units are often incorporated into polymeric membranes for CO2 separations, high-molecular-weight poly(ethylene oxide) (high-M-w PEO) cannot be used effectively due to its inferior separation performance, despite its good solubility in mild solvents (e.g. water and alcohols) and commercial availability at low cost. A high-performance, defect-free membrane for CO2 separations based on high-M-w PEO was prepared by incorporating the crosslinkable poly(glycidyl methacrylate-g-polypropylene glycol)-co-poly(oxyethylene methacrylate) (PGP-POEM) comb copolymer. The CO2/N-2 and CO2/CH4 selectivity of the neat high-M-w PEO membrane was as low as 0.8 and 0.6, respectively, which increased drastically with increasing comb copolymer content, and the thermal and mechanical properties were also improved. The three-dimensionally interweaved network of the comb copolymer occurred within the PEO matrix, which had a considerable effect on the crystalline structure of the membranes. The crystalline morphology of the membranes and the distribution of comb copolymer within the PEO matrix were comprehensively examined according to the comb copolymer content. The comb copolymer effectively suppressed the formation of non-selective defects by filling the interlamellar and interfibrillar regions of the PEO crystallites. The best separation performance was achieved with a comb copolymer loading of 30 wt%, showing a CO2 permeability of 120.9 barrer with CO2/N-2 and CO2/CH4 selectivity of 44.9 and 14.5, respectively. The tensile strength and elongation at break reached 7.5 MPa and 1490%, respectively. This work presents an avenue for utilizing a low-cost, commercially-available, high-M-w PEO in gas separation applications, providing insight into the crystalline structure and morphology of these membranes.

Improving CO2 separation performance of PEGDME-PVDF/PP composite membrane

Improving CO 2 separation performance of the polyethylene glycol (PEG)/polytrifluoropropylsiloxane (PTFPMS) blend composite membrane

Towards enhanced CO2 selectivity of the PIM-1 membrane by blending with polyethylene glycol

Improving CO2 Permeation and Separation Performance of CO2-philic Polymer Membrane by Blending CO2 Absorbents

Enhanced Co2 Separation Properties by Incorporating Poly(Ethylene Glycol)-Containing Polymeric Submicrospheres into Polyimide Membrane

Carbon Dioxide Separation by Polyethylene Glycol and Glutamic Acid/Polyvinyl Alcohol Composite Membrane

Preparation of Hollow Fiber Poly(n,n-Dimethylaminoethyl Methacrylate)–poly(ethylene Glycol Methyl Ether Methyl Acrylate)/polysulfone Composite Membranes for CO2/N2 Separation

Facilitated transport of CO2 through polyvinylamine/polyethlene glycol blend membranes

Dialdehyde Polyethylene Glycol Cross‐linked Poly(vinyl Alcohol) Membranes with Enhanced CO2/N2 Separation Performance

Use of Non-Selective, High-Molecular-weight Poly(ethylene Oxide) Membrane for CO2 Separation by Incorporation of Comb Copolymer

Facile Fabrication of Co2 Separation Membranes by Cross-Linking of Poly(Ethylene Glycol) Diglycidyl Ether with A Diamine and A Polyamine-Based Ionic Liquid

Facile and solvent-free fabrication of PEG-based membranes with interpenetrating networks for CO2 separation

Preparation and Separation Performance of PDMS Composite Membranes for CO2 Separation from CO2-DMC System

Performance of poly(vinyl alcohol)-poly(ethylene imine) blend membrane for separation of dimethyl carbonate and CO_2

Fabrication and Characterization of Poly(vinylidene Fluoride)–polytetrafluoroethylene Composite Membrane for CO2 Absorption in Gas–liquid Contacting Process

Enhanced CO2 Selectivities by Incorporating CO2-philic PEG-POSS into Polymers of Intrinsic Microporosity Membrane

The Effects of PEI Hollow Fiber Substrate Characteristics on PDMS/PEI Hollow Fiber Membranes for CO2/N2 Separation

Effects of Preparation Parameters on CO2/N-2 Gas Permselectivity of Polyether Thin Film Composite Membrane

Interfacially polymerized polyetheramine thin film composite membranes with PDMS inter-layer for CO2 separation

Enhanced Gas Separation Performance by Embedding Submicron Poly(ethylene Glycol) Capsules into Polyetherimide Membrane

Poly(ethylene oxide)-Based Copolymer-IL Composite Membranes for CO2 Separation