Abstract:Despite numerous studies focused on the hydrothermal (HT) synthesis of fly ash zeolites (FAZs), this method still has many limitations, the main of which is the low yield of zeolites. Hydrothermally synthesized zeolites are typically multiphase and exhibit low purity, which limits their applicability. Pure-phase zeolites have been primarily prepared from filtrates after alkaline mineralization of fly ashes, not directly in suspension. In addition, the published methodologies have not been tested in a wider set of samples, and thus their reproducibility is not confirmed. The aim of the study is to propose a reproducible methodology that overcomes the mentioned limitations. The influence of the Si/Al ratio (1.3:1–1:2), the type and concentration of the activator (2/4 M NaOH/KOH/LiOH), the reagent (30% LiCl), the duration (24–168 h), and the temperature (50–180 °C) of the synthesis phases were studied. The sequence of the synthesis phases was also optimized, depending on the type of heat transfer. The fly ashes were analyzed by wavelength-dispersive X-ray fluorescence (WD XRF), flame atomic absorption spectrometry (F-AAS), and X-ray diffraction (XRD). The energy intensity of the synthesis was reduced through the application of unique microwave digestion technology. Both microwave and combined (microwave and convection) syntheses were conducted. FAZs were identified and quantified by XRD analysis. This study presents a three-stage (TS) hydrothermal synthesis of pure-phase sodalite in suspension. Sodalite (>99 wt.%) was prepared from nine fly ashes under the following conditions: I. microwave phase: 120 °C, 150 min, solid-to-liquid ratio (S/L) 1:5, Si/Al ratio 1:1.5, and 4 M NaOH; II. convection phase: 120 °C, 24 h, S/L 1:40, and the addition of 30 mL of 30% LiCl; and III. crystallization: 70 °C for 24 h. The formation of rhombododecahedral sodalite crystals was confirmed by scanning electron microscope (SEM) images.

Hydrothermal Synthesis of Acicular Wollastonite from Potassium Silicate Solution

Structure, morphology and mechanism research on synthesizing xonotlite fiber from acid-extracting residues of coal fly ash and carbide slag

Simple and rapid synthesis of zeolite W from K‐feldspar via the improved hydrothermal method

Hydrothermal Synthesis of Zeolite A from K-feldspar and Its Crystallization Mechanism

Hydrothermal extraction of potassium from potassic quartz syenite and preparation of aluminum hydroxide

Synthesis of Pure-Silica Mtw Powder and Supported Films

Preparation of potassium sulfate and zeolite NaA from K-feldspar by a novel hydrothermal process

Control of crystallization rate and morphology of zeolite silicalite-1 in solvent-free synthesis

Synthesis and Characterization of Lanthanum Hydroxide by Hydrothermal Method

Hydrothermal Synthesis of K-ZSM-5 Molecular Sieve from Potassium Feldspar

Hydrothermal/Alkali Fusion Synthesis of Zeolite NaA and NaX from Pyrophyllite Mineral Clay

Study on the Mechanism of Rapid Synthesis of Small Grain NaX Type Molecular Sieve with Calcined Kaolin

The Effect of Oxalic Acid and Citric Acid on the Modification of Wollastonite Surface

Alkli-activated Mechanisms of Kaolinite and Hydrothermal Synthesis of 4A Zeolite

Synthesis of pure zeolite X from coal slime

Zeolite-X synthesized from halloysite nanotubes and its application in CO2 capture

Manipulation of the Crystallization of Ssz-13 Transformed from Coal Fly Ash-Derived Analcime

Synthesis of White Mineral Trioxide Aggregate (WMTA) Using Silica from Rice Husk Ash and CaCO3 from Limestone

Microwave-Assisted Hydrothermal Synthesis of Pure-Phase Sodalite (>99 wt.%) in Suspension: Methodology Design and Verification

Controllable and SDA-free synthesis of sub-micrometer sized zeolite ZSM-5. Part 1: Influence of alkalinity on the structural, particulate and chemical properties of the products

Synthesis of Tungsten Trioxide and Lithiated Tungsten Oxides by a Soft Chemistry Route and Their Structural Stability